Comparative Analysis of Weld Microstructure in Ti-6Al-4V Samples Produced by Rolling and Wire-Feed Electron Beam Additive Manufacturing; Physical Mesomechanics; Vol. 26, iss. 6

Comparative Analysis of Weld Microstructure in Ti-6Al-4V Samples Produced by Rolling and Wire-Feed Electron Beam Additive Manufacturing; Physical Mesomechanics; Vol. 26, iss. 6

Bibliographic Details
Parent link:Physical Mesomechanics.— .— New York: Springer Science+Business Media LLC.
Vol. 26, iss. 6.— 2023.— P. 643-655
Corporate Author: Томский политехнический университет
Other Authors: Panin A. V. Alexey Viktorovich, Kazachenok M. S. Marina Sergeevna, Krukovsky K. V. Konstantin Vitaljevich, Kazantseva L. A. Lyudmila Aleseevna, Martynov S. A. Sergey Andreevich
Summary:Title screen
The microstructure and phase composition of electron beam welded Ti-6Al-4V titanium alloy were studied by optical and scanning electron microscopy, backscattered electron diffraction, and X-ray diffraction analysis. Deep-penetration electron beam welds were made in a single pass on rectangular Ti-6Al4V samples obtained by rolling and wire-feed electron beam additive manufacturing. It was found that the weld width in the 3D printed Ti-6Al-4V samples is greater than in the rolled material. The influence of the vapor capillary on the size, shape and structure of primary β grains formed in the fusion zone was shown. The variation of the penetration coefficient, volume fraction of the residual β phase, and residual stresses along the weld length was studied for Ti-6Al-4V samples obtained by both rolling and 3D printing
Текстовый файл
AM_Agreement
Language:English
Published: 2023
Subjects:
электронный ресурс
труды учёных ТПУ
Ti-6Al-4V
titanium alloy
electron beam welding
deep-penetration keyhole welding
additive manufacturing technology
microstructure
microhardness
Online Access:https://doi.org/10.1134/S1029959923060048
Format: Electronic Book Chapter
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=672021