The Microstructural and Phase Evolution of the 3D Printed Ti-6Al-4V Alloy during Mechanical Loading
Збережено в:
| Parent link: | Physics of Metals and Metallography Vol. 124, iss. 2.— 2023.— [P. 217-223] |
|---|---|
| Інші автори: | , , , , |
| Резюме: | Title screen This paper presents the results of an in situ study on the evolution of the microstructure and phase composition of 3D-printed Ti-6Al-4V samples under tension in the transmission electron microscope column. The microstructure of Ti-6Al-4V specimens manufactured by wire-feed electron beam additive technology is shown to consist of columnar primary β-grains inside of which are α/α'-Ti laths separated by layers of the residual β-phase and gathered into packets. A characteristic feature of 3D-printed Ti-6Al-4V samples is the concentration nonuniformity of the alloying elements due to the partial decomposition of the martensitic α'-phase. The reorientation of the α/α'-Ti lattice near interfaces takes place during uniaxial tension. Deformation-induced α'→α" transformations can develop in the reoriented regions of the α/α'-Ti lattice, in places enriched in vanadium. Режим доступа: по договору с организацией-держателем ресурса |
| Мова: | Англійська |
| Опубліковано: |
2023
|
| Предмети: | |
| Онлайн доступ: | https://doi.org/10.1134/S0031918X23700114 |
| Формат: | Електронний ресурс Частина з книги |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=669586 |
| Теги: |
Додати тег
Немає тегів, Будьте першим, хто поставить тег для цього запису!
|