Surface Treatments and Residual Stress: Assessing the Implications for Biocompatibility in Titanium Implants; Russian Physics Journal; Vol. 66, iss. 1

Surface Treatments and Residual Stress: Assessing the Implications for Biocompatibility in Titanium Implants; Russian Physics Journal; Vol. 66, iss. 1

Bibliografiska uppgifter
Parent link:Russian Physics Journal
Vol. 66, iss. 1.— 2023.— [P. 116-123]
Huvudupphovsman: Prosolov K. A. Konstantin Aleksandrovich
Institutionell upphovsman: Национальный исследовательский Томский политехнический университет Исследовательская школа физики высокоэнергетических процессов
Övriga upphovsmän: Khimich M. A. Margarita Andreevna, Sharkeev Yu. P. Yury Petrovich
Sammanfattning:Title screen
The interaction between implanted materials and body tissues at the cellular level is a critical factor for the success of biomedical implants. Surface modifications, including grinding, polishing, abrasive blasting, and chemical etching together with the application of bioactive coatings such as calcium phosphates are commonly employed to improve implant performance. Each surface treatment alters the topology, roughness, and residual mechanical stresses in the material which can affect cellular responses. In this study, we examine the impact of various surface treatments on the surface morphology, stress state, and elemental composition of titanium alloy samples comparable to commercially available implants. The residual stress values, measured using XRD, have been found to be 400 ± 5 MPa for polished samples, 350 ± 10 MPa for rolled samples, 345 ± 5 MPa for abrasive blasted samples, 215 ± 3 MPa for etched samples, and 260 ± 10 MPa for coated samples. Given the potential influence of residual stress gradients on cell behavior, it is important to consider the stress state as a criterion for implant biocompatibility. Further investigation into the relationship between the residual stress and the cellular responses will contribute to the development of more effective implant materials and surface treatments, ultimately enhancing osseointegration and overall implant performance. This study highlights the need for a comprehensive understanding of the role of the residual stress in implant biocompatibility and suggests a novel direction for future research in this field.
Режим доступа: по договору с организацией-держателем ресурса
Språk:engelska
Publicerad: 2023
Ämnen:
электронный ресурс
труды учёных ТПУ
stress state
surface treatment
implants
biocompatibility
antibacterial activity
Länkar:https://doi.org/10.1007/s11182-023-02912-5