Thermal analysis of Co-Zn ferrite synthesis from milled powders
| Parent link: | Journal of Thermal Analysis and Calorimetry Vol. 148.— 2023.— [P. 1455-1462] |
|---|---|
| مؤلفون مشاركون: | , |
| مؤلفون آخرون: | , , , |
| الملخص: | Title screen The effect of mechanical activation of the mixture of Fe2O3-Co3O4-ZnO reagents on thermal synthesis of cobalt-zinc ferrite (Co0.5Zn0.5Fe2O4) was studied using X-ray powder diffraction and thermal analyses. The initial oxide powders were mixed using a Retsch Emax high energy ball mill to homogenize the mixture and enhance the reactivity. Mechanical activation was performed in air for 30 and 60 min. Thermal synthesis was performed at 900 °C for 4 h. X-ray diffraction analysis revealed an increase in the intensity of reflections that belong to spinel phases at increased rotational speed of the grinding vials and grinding duration. The patterns of formation of the final ferrite phase depending on the modes of mechanical pre-activation were showed by thermal analysis. It was shown that mechanical pre-activation of a mixture of initial reagents in a high-energy ball mill facilitates the formation of the ferrite phase of the given composition. The Curie temperature was determined for Co0.5Zn0.5Fe2O4 ferrite (~ 178 °C) by thermal synthesis. Kindly check and confirm whether the corresponding author is correctly identified. Corresponding author identified correctly. Режим доступа: по договору с организацией-держателем ресурса |
| اللغة: | الإنجليزية |
| منشور في: |
2023
|
| الموضوعات: | |
| الوصول للمادة أونلاين: | https://doi.org/10.1007/s10973-022-11807-5 |
| التنسيق: | الكتروني فصل الكتاب |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=669171 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 669171 | ||
| 005 | 20250214164519.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\40411 | ||
| 035 | |a RU\TPU\network\39764 | ||
| 090 | |a 669171 | ||
| 100 | |a 20230220d2023 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a NL | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Thermal analysis of Co-Zn ferrite synthesis from milled powders |f E. V. Nikolaev, E. N. Lysenko, A. P. Surzhikov, A. L. Astafjev | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 31 tit.] | ||
| 330 | |a The effect of mechanical activation of the mixture of Fe2O3-Co3O4-ZnO reagents on thermal synthesis of cobalt-zinc ferrite (Co0.5Zn0.5Fe2O4) was studied using X-ray powder diffraction and thermal analyses. The initial oxide powders were mixed using a Retsch Emax high energy ball mill to homogenize the mixture and enhance the reactivity. Mechanical activation was performed in air for 30 and 60 min. Thermal synthesis was performed at 900 °C for 4 h. X-ray diffraction analysis revealed an increase in the intensity of reflections that belong to spinel phases at increased rotational speed of the grinding vials and grinding duration. The patterns of formation of the final ferrite phase depending on the modes of mechanical pre-activation were showed by thermal analysis. It was shown that mechanical pre-activation of a mixture of initial reagents in a high-energy ball mill facilitates the formation of the ferrite phase of the given composition. The Curie temperature was determined for Co0.5Zn0.5Fe2O4 ferrite (~ 178 °C) by thermal synthesis. Kindly check and confirm whether the corresponding author is correctly identified. Corresponding author identified correctly. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | |t Journal of Thermal Analysis and Calorimetry | ||
| 463 | |t Vol. 148 |v [P. 1455-1462] |d 2023 | ||
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a cobalt-zinc ferrite | |
| 610 | 1 | |a mechanical milling | |
| 610 | 1 | |a solid-state synthesis | |
| 610 | 1 | |a thermal analysis | |
| 610 | 1 | |a X-ray powder diffraction | |
| 701 | 1 | |a Nikolaev |b E. V. |c specialist in the field of electrical engineering |c engineer of Tomsk Polytechnic University |f 1989- |g Evgeny Vladimirovich |3 (RuTPU)RU\TPU\pers\34529 |9 17910 | |
| 701 | 1 | |a Lysenko |b E. N. |c Specialist in the field of electrical engineering |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1972- |g Elena Nikolaevna |3 (RuTPU)RU\TPU\pers\32050 |9 16097 | |
| 701 | 1 | |a Surzhikov |b A. P. |c physicist |c Professor of Tomsk Polytechnic University, doctor of physical and mathematical sciences (DSc) |f 1951- |g Anatoly Petrovich |3 (RuTPU)RU\TPU\pers\30237 |9 14617 | |
| 701 | 1 | |a Astafjev |b A. L. |g Aleksandr Leonidovich | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Институт неразрушающего контроля |b Проблемная научно-исследовательская лаборатория электроники, диэлектриков и полупроводников |3 (RuTPU)RU\TPU\col\19033 |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Инженерная школа неразрушающего контроля и безопасности |b Отделение контроля и диагностики |3 (RuTPU)RU\TPU\col\23584 |
| 801 | 0 | |a RU |b 63413507 |c 20230220 |g RCR | |
| 856 | 4 | |u https://doi.org/10.1007/s10973-022-11807-5 | |
| 942 | |c CF | ||