A comprehensive study of the structure and piezoelectric response of biodegradable polyhydroxybutyrate-based films for tissue engineering applications; Polymer Journal; Vol. 54

التفاصيل البيبلوغرافية
Parent link:	Polymer Journal Vol. 54.— 2022.— [P. 1225-1236]
مؤلف مشترك:	Национальный исследовательский Томский политехнический университет Исследовательская школа химических и биомедицинских технологий Научно-исследовательский центр "Физическое материаловедение и композитные материалы"
مؤلفون آخرون:	Chernozem R. V. Roman Viktorovich, Pary (Pariy) I. O. Igor Olegovich, Pryadko A. Artyom, Bonartsev A. P. Anton Pavlovich, Voinova V. V. Vera Vladimirovna, Zhuykov V. A. Vsevolod Aleksandrovich, Makhina T. Tatjyana, Bonartseva G. A. Garina Aleksandrovna, Shaytan K. V. Konstantin Voldemarovich, Shvartsman V. V. Vladimir, Lupascu D. C. Doru, Romanyuk K. N., Kholkin A. L. Andrei Leonidovich, Surmenev R. A. Roman Anatolievich, Surmeneva M. A. Maria Alexandrovna
الملخص:	Title screen The results of comprehensive research on the thermal behavior and molecular and crystalline structures of poly(3-hydroxybutyrate) (PHB) and poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHB-HV) films of different thicknesses, their molecular weights (Mw) and 3-hydroxyvalerate (3-HV) contents are reported. Increasing film thickness from 30 to 100 µm resulted in an isotropic crystal orientation, reducing the crystallite size of the orthorhombic α-phase in the b direction from 22 to 17 nm and increasing the degree of crystallinity of the PHB films without affecting their thermal behavior. Furthermore, despite resulting in the same degree of crystallinity and roughness, an ~8-fold decrease in PHB Mw from 803 kDa to 102 kDa resulted in a decreased number of piezoactive domains. The addition of 5.9% 3-HV resulted in anisotropy in the PHB crystalline structure and increased D(020) from 19 nm to 24 nm. Additionally, a further increase in the 3-HV content to 17.5% in the PHB-HV films led to a decrease in the melting temperature and a decrease in the degree of crystallinity from 57% to 23%, which resulted in the absence of local piezoresponse. Notably, the decrease in the Mw of PHB-HV (~17%) from 1177 kDa to 756 kDa resulted in an increase in the degree of crystallinity from 23% to 32%. Moreover, the PHB-HV films became smoother with increasing 3-HV content. Режим доступа: по договору с организацией-держателем ресурса
اللغة:	الإنجليزية
منشور في:	2022
الموضوعات:	электронный ресурс труды учёных ТПУ biomedical materials polymer characterization биомедицинские материалы полимеры
الوصول للمادة أونلاين:	https://doi.org/10.1038/s41428-022-00662-8