Macrosegmentation and strain hardening stages in copper single crystals under compression; International Journal of Plasticity; Vol. 69

Λεπτομέρειες βιβλιογραφικής εγγραφής
Parent link:International Journal of Plasticity
Vol. 69.— 2015.— [P. 36-53]
Συλλογικό Έργο: Томский политехнический университет Юргинский технологический институт, Национальный исследовательский Томский политехнический университет Инженерная школа новых производственных технологий, Национальный исследовательский Томский политехнический университет Физико-технический институт Лаборатория № 33 ядерного реактора
Άλλοι συγγραφείς: Lychagin D. V. Dmitry Vasilievich, Tarasov S. Yu. Sergei Yulievich, Chumaevsky A. V. Andrey Valerjevich, Alferova (Alfyorova) E. A. Ekaterina Aleksandrovna
Περίληψη:Title screen
The surface deformation-induced pattern (relief) of copper single crystals with the orientation of the compression axis along [11¯1¯] has been investigated by means of optical, scanning electron and atomic force microscopy. The misorientations between both macroscopic and mesoscopic areas in [11¯1¯]-single crystals have been determined using the electron back scattering diffraction (EBSD) technique. The macroscopic reorientation has been revealed to rotate the crystalline lattice around the [110] axis. The single crystal has been divided into five macrosegments with their misorientations distributed along the compression axis in a manner that the deformation axis sequentially coincided with the crystallographic directions in the order [11¯1¯]-[22¯1¯]-[77¯3¯]-[11¯0]. Shear by unloaded plane (11¯1¯) has been observed. The macrolevel deformation up to 25% has been developing as follows: shear by octahedral planes - development of macrobands - reorientation of the central zones - shear by unloaded octahedral plane in the reoriented zones. The steps of this sequence corresponded to the stages of the stress-strain curves.
Режим доступа: по договору с организацией-держателем ресурса
Γλώσσα:Αγγλικά
Έκδοση: 2015
Θέματα:
Διαθέσιμο Online:https://doi.org/10.1016/j.ijplas.2015.01.007
Μορφή: MixedMaterials Ηλεκτρονική πηγή Κεφάλαιο βιβλίου
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=667774

MARC

LEADER 00000naa0a2200000 4500
001 667774
005 20250527134939.0
035 |a (RuTPU)RU\TPU\network\38985 
035 |a RU\TPU\network\9843 
090 |a 667774 
100 |a 20220420d2015 k||y0rusy50 ba 
101 0 |a eng 
102 |a NL 
135 |a drcn ---uucaa 
181 0 |a i  
182 0 |a b 
200 1 |a Macrosegmentation and strain hardening stages in copper single crystals under compression  |f D. V. Lychagin, S. Yu. Tarasov, A. V. Chumaevsky, E. A. Alfyorova 
203 |a Текст  |c электронный 
300 |a Title screen 
320 |a [References: p. 51-53] 
330 |a The surface deformation-induced pattern (relief) of copper single crystals with the orientation of the compression axis along [11¯1¯] has been investigated by means of optical, scanning electron and atomic force microscopy. The misorientations between both macroscopic and mesoscopic areas in [11¯1¯]-single crystals have been determined using the electron back scattering diffraction (EBSD) technique. The macroscopic reorientation has been revealed to rotate the crystalline lattice around the [110] axis. The single crystal has been divided into five macrosegments with their misorientations distributed along the compression axis in a manner that the deformation axis sequentially coincided with the crystallographic directions in the order [11¯1¯]-[22¯1¯]-[77¯3¯]-[11¯0]. Shear by unloaded plane (11¯1¯) has been observed. The macrolevel deformation up to 25% has been developing as follows: shear by octahedral planes - development of macrobands - reorientation of the central zones - shear by unloaded octahedral plane in the reoriented zones. The steps of this sequence corresponded to the stages of the stress-strain curves. 
333 |a Режим доступа: по договору с организацией-держателем ресурса 
461 |t International Journal of Plasticity 
463 |t Vol. 69  |v [P. 36-53]  |d 2015 
610 1 |a электронный ресурс 
610 1 |a труды учёных ТПУ 
610 1 |a single crystal 
610 1 |a copper 
610 1 |a stress-strain curves 
610 1 |a surface deformation pattern 
610 1 |a electron backscattered diffraction 
610 1 |a монокристаллы 
610 1 |a медь 
610 1 |a напряжение 
610 1 |a деформации 
610 1 |a поверхности 
610 1 |a рассеянные электроны 
701 1 |a Lychagin  |b D. V.  |c specialist in the field of mechanical engineering  |c Professor of Yurga technological Institute of Tomsk Polytechnic University, Doctor of physical and mathematical sciences  |f 1957-  |g Dmitry Vasilievich  |3 (RuTPU)RU\TPU\pers\31402  |9 15574 
701 1 |a Tarasov  |b S. Yu.  |c specialist in the field of mechanical engineering  |c Professor of Tomsk Polytechnic University, Doctor of technical sciences  |f 1959-  |g Sergei Yulievich  |3 (RuTPU)RU\TPU\pers\31400  |9 15572 
701 1 |a Chumaevsky  |b A. V.  |g Andrey Valerjevich 
701 1 |a Alferova (Alfyorova)  |b E. A.  |c specialist in the field of mechanical engineering  |c associate Professor Yurginsky technological Institute (branch) of Tomsk Polytechnic University, candidate of physical and mathematical Sciences  |f 1982-  |g Ekaterina Aleksandrovna  |3 (RuTPU)RU\TPU\pers\34576  |9 17938 
712 0 2 |a Томский политехнический университет  |b Юргинский технологический институт  |c (2003-2009)  |3 (RuTPU)RU\TPU\col\12451  |9 25408 
712 0 2 |a Национальный исследовательский Томский политехнический университет  |b Инженерная школа новых производственных технологий  |c (2017- )  |3 (RuTPU)RU\TPU\col\23501 
712 0 2 |a Национальный исследовательский Томский политехнический университет  |b Физико-технический институт  |b Лаборатория № 33 ядерного реактора  |3 (RuTPU)RU\TPU\col\19896 
801 0 |a RU  |b 63413507  |c 20220420  |g RCR 
850 |a 63413507 
856 4 |u https://doi.org/10.1016/j.ijplas.2015.01.007  |z https://doi.org/10.1016/j.ijplas.2015.01.007 
942 |c CF