Testing of the Ti foil with TiN coating as an exit window of a pulsed electron accelerator; Vacuum; Vol. 199
| Parent link: | Vacuum Vol. 199.— 2022.— [110921, 5 p.] |
|---|---|
| Corporate Authors: | , |
| 其他作者: | , , , |
| 總結: | Title screen Testing of the Ti foil with TiN coating as an exit window of a pulsed electron accelerator Increasing the efficiency of electron beam extraction from a vacuum diode is an urgent problem for the practical use of accelerators. In the general case, the given problem is reduced to decreasing the mass thickness (g/cm2) of the exit window membrane while ensuring sufficient mechanical properties. The paper presents the results of testing an exit window 85 mm in diameter with a 25 μm Ti membrane and a 0.8 μm TiN coating. When tested, the coated membrane exhibited mechanical characteristics comparable to those of a 60 μm Ti membrane, which deteriorated upon repeated pumpings of the accelerator chamber volume due to the appearance of cracks in the coating. The energy loss of the electron beam in the exit window of the accelerator was decreased by 18%, as compared to the Ti 60 μm membrane. The use of a 25 μm Ti membrane with a 0.8 μm TiN coating provided 16 J per pulse energy output of more than 104 pulses of the electron beam (50-275 keV) with a repetition rate of 1-10 pulses per second. The obtained results will be used to further improve the electron beam extraction systems in the field of high-pressure applications. Режим доступа: по договору с организацией-держателем ресурса |
| 語言: | 英语 |
| 出版: |
2022
|
| 主題: | |
| 在線閱讀: | https://doi.org/10.1016/j.vacuum.2022.110921 |
| 格式: | 電子 Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=667276 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 667276 | ||
| 005 | 20260317071600.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\38481 | ||
| 035 | |a RU\TPU\network\38213 | ||
| 090 | |a 667276 | ||
| 100 | |a 20220314d2022 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Testing of the Ti foil with TiN coating as an exit window of a pulsed electron accelerator |f I. S. Egorov, E. A. Smolyanskiy, A. V. Poloskov, M. A. Serebrennikov | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 31 tit.] | ||
| 330 | |a Testing of the Ti foil with TiN coating as an exit window of a pulsed electron accelerator Increasing the efficiency of electron beam extraction from a vacuum diode is an urgent problem for the practical use of accelerators. In the general case, the given problem is reduced to decreasing the mass thickness (g/cm2) of the exit window membrane while ensuring sufficient mechanical properties. The paper presents the results of testing an exit window 85 mm in diameter with a 25 μm Ti membrane and a 0.8 μm TiN coating. When tested, the coated membrane exhibited mechanical characteristics comparable to those of a 60 μm Ti membrane, which deteriorated upon repeated pumpings of the accelerator chamber volume due to the appearance of cracks in the coating. The energy loss of the electron beam in the exit window of the accelerator was decreased by 18%, as compared to the Ti 60 μm membrane. The use of a 25 μm Ti membrane with a 0.8 μm TiN coating provided 16 J per pulse energy output of more than 104 pulses of the electron beam (50-275 keV) with a repetition rate of 1-10 pulses per second. The obtained results will be used to further improve the electron beam extraction systems in the field of high-pressure applications. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | |t Vacuum | ||
| 463 | |t Vol. 199 |v [110921, 5 p.] |d 2022 | ||
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a vacuum electron diode | |
| 610 | 1 | |a electron beam extraction | |
| 610 | 1 | |a accelerator exit window | |
| 610 | 1 | |a sealing membrane | |
| 610 | 1 | |a вакуумные диоды | |
| 610 | 1 | |a экстракция | |
| 610 | 1 | |a электронные диоды | |
| 610 | 1 | |a электронные лучи | |
| 610 | 1 | |a выходное окно | |
| 610 | 1 | |a ускорители | |
| 610 | 1 | |a мембраны | |
| 610 | 1 | |a фольга | |
| 610 | 1 | |a покрытия | |
| 701 | 1 | |a Egorov |b I. S. |c physicist |c Researcher of Tomsk Polytechnic University, Candidate of technical sciences |f 1985- |g Ivan Sergeevich |y Tomsk |3 (RuTPU)RU\TPU\pers\32792 |9 16650 | |
| 701 | 1 | |a Smolyanskiy (Smolyansky, Smolyanskii) |b E. A. |c Physicist |c Research Engineer of Tomsk Polytechnic University |f 1985- |g Egor Aleksandrovich |3 (RuTPU)RU\TPU\pers\37673 |9 20478 | |
| 701 | 1 | |a Poloskov |b A. V. |c physicist |c Engineer of Tomsk Polytechnic University |f 1990- |g Artem Viktorovich |3 (RuTPU)RU\TPU\pers\32794 |9 16652 | |
| 701 | 1 | |a Serebrennikov |b M. A. |c Physicist |c Engineer of Tomsk Polytechnic University |f 1995- |g Maksim Anatolevich |3 (RuTPU)RU\TPU\pers\43059 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Инженерная школа новых производственных технологий |b Научно-производственная лаборатория "Импульсно-пучковых, электроразрядных и плазменных технологий" |3 (RuTPU)RU\TPU\col\23502 |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Исследовательская школа физики высокоэнергетических процессов |c (2017- ) |3 (RuTPU)RU\TPU\col\23551 |
| 801 | 2 | |a RU |b 63413507 |c 20220314 |g RCR | |
| 856 | 4 | |u https://doi.org/10.1016/j.vacuum.2022.110921 | |
| 942 | |c CF | ||