Defects level evaluation of LiTiZn ferrite ceramics using temperature dependence of initial permeability; Journal of Magnetism and Magnetic Materials; Vol. 456

Defects level evaluation of LiTiZn ferrite ceramics using temperature dependence of initial permeability; Journal of Magnetism and Magnetic Materials; Vol. 456

Dettagli Bibliografici
Parent link:Journal of Magnetism and Magnetic Materials
Vol. 456.— 2018.— [P. 186-193]
Ente Autore: Национальный исследовательский Томский политехнический университет Инженерная школа неразрушающего контроля и безопасности Отделение контроля и диагностики
Altri autori: Malyshev A. V. Andrei Vladimirovich, Petrova A. B. Anna Borisovna, Sokolovsky A. N. Aleksey Nikolaevich, Surzhikov A. P. Anatoly Petrovich
Riassunto:Title screen
The method for evaluating the integral defects level and chemical homogeneity of ferrite ceramics based on temperature dependence analysis of initial permeability is suggested. A phenomenological expression for the description of such dependence was suggested and an interpretation of its main parameters was given. It was shown, that the main criterion of the integral defects level of ferrite ceramics is relation of two parameters correlating with elastic stress value in a material. An indicator of structural perfection can be a maximum value of initial permeability close to Curie point as well. The temperature dependences of initial permeability have analyzed for samples sintered in laboratory conditions and for the ferrite industrial product. The proposed method allows controlling integral defects level of the soft ferrite products and has high sensitivity compare to typical X-ray methods.
Режим доступа: по договору с организацией-держателем ресурса
Lingua:inglese
Pubblicazione: 2018
Soggetti:
электронный ресурс
труды учёных ТПУ
дефекты
керамика
температурные зависимости
проницаемость
Accesso online:https://doi.org/10.1016/j.jmmm.2018.02.032
Natura: Elettronico Capitolo di libro
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=666769