Properties of Bitumen Composition Modified by Petroleum Resins; Журнал Сибирского федерального университета. Серия: Химия; Т. 14, № 2
| Parent link: | Журнал Сибирского федерального университета. Серия: Химия=Journal of Siberian Federal University. Chemistry/ Сибирский федеральный университет (СФУ).— , 2008- Т. 14, № 2.— 2021.— [С. 147-155] |
|---|---|
| Συγγραφή απο Οργανισμό/Αρχή: | |
| Άλλοι συγγραφείς: | , , , |
| Περίληψη: | Title screen It was advised to use aliphatic, cycloaliphatic, aromatic petroleum resins and their derivatives obtained by oxidation of resins with a mixture of hydrogen peroxide and acetic acid as bitumen polymer-modifiers. Petroleum resins were obtained by ionic polymerization of unsaturated compounds of liquid pyrolysis products under the influence of titanium tetrachloride-diethylaluminium chloride catalyst. It was established that the maximum values of adhesion of modified bitumen coatings to metal substrates, corresponding to the minimum values of the wetting angle of the metal surface coated with solutions of bitumen compositions with different content of the polymer modifier were achieved using oxidized resins. All modified bitumen coatings have low water absorptivity and high acid resistance, alkali resistance and salt resistance, which allow using them as protective coatings. Показано использование алифатических, циклоалифатических, ароматических нефтеполимерных смол, полученных ионной полимеризацией непредельных соединений различных фракций жидких продуктов пиролиза под действием каталитической системы тетрахлорид титана - диэтилалюминийхлорид и их окисленных смесью пероксида водорода и уксусной кислоты производных в качестве полимеров-модификаторов битума. Установлено, что максимальные значения адгезии модифицированных битумных покрытий к металлическим подложкам, соответствующие минимальным значениям краевого угла смачивания подложек битумным раствором, достигнуты при использовании окисленных смол. Все модифицированные битумные покрытия обладают низким водопоглощением и высокой кислото-, щелоче- и солестойкостью, что позволяет использовать их в качестве защитных покрытий. Режим доступа: по договору с организацией-держателем ресурса |
| Γλώσσα: | Ρωσικά |
| Έκδοση: |
2021
|
| Θέματα: | |
| Διαθέσιμο Online: | http://dx.doi.org/10.17516/1998-2836-0224 |
| Μορφή: | Ηλεκτρονική πηγή Κεφάλαιο βιβλίου |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=666444 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 666444 | ||
| 005 | 20250215171423.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\37648 | ||
| 035 | |a RU\TPU\network\36329 | ||
| 090 | |a 666444 | ||
| 100 | |a 20211224d2021 k||y0rusy50 ba | ||
| 101 | 0 | |a rus | |
| 102 | |a RU | ||
| 135 | |a drgn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Properties of Bitumen Composition Modified by Petroleum Resins |d Свойства битумных композиций, модифицированных нефтеполимерными смолами |f V. G. Bondaletov, L. I. Bondaletova, Nguyen Van Thanh, A. V. Bondaletova | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 20 tit.] | ||
| 330 | |a It was advised to use aliphatic, cycloaliphatic, aromatic petroleum resins and their derivatives obtained by oxidation of resins with a mixture of hydrogen peroxide and acetic acid as bitumen polymer-modifiers. Petroleum resins were obtained by ionic polymerization of unsaturated compounds of liquid pyrolysis products under the influence of titanium tetrachloride-diethylaluminium chloride catalyst. It was established that the maximum values of adhesion of modified bitumen coatings to metal substrates, corresponding to the minimum values of the wetting angle of the metal surface coated with solutions of bitumen compositions with different content of the polymer modifier were achieved using oxidized resins. All modified bitumen coatings have low water absorptivity and high acid resistance, alkali resistance and salt resistance, which allow using them as protective coatings. | ||
| 330 | |a Показано использование алифатических, циклоалифатических, ароматических нефтеполимерных смол, полученных ионной полимеризацией непредельных соединений различных фракций жидких продуктов пиролиза под действием каталитической системы тетрахлорид титана - диэтилалюминийхлорид и их окисленных смесью пероксида водорода и уксусной кислоты производных в качестве полимеров-модификаторов битума. Установлено, что максимальные значения адгезии модифицированных битумных покрытий к металлическим подложкам, соответствующие минимальным значениям краевого угла смачивания подложек битумным раствором, достигнуты при использовании окисленных смол. Все модифицированные битумные покрытия обладают низким водопоглощением и высокой кислото-, щелоче- и солестойкостью, что позволяет использовать их в качестве защитных покрытий. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | |t Журнал Сибирского федерального университета. Серия: Химия |l Journal of Siberian Federal University. Chemistry |f Сибирский федеральный университет (СФУ) |d 2008- | ||
| 463 | |t Т. 14, № 2 |v [С. 147-155] |d 2021 | ||
| 510 | 1 | |a Свойства битумных композиций, модифицированных нефтеполимерными смолами |z rus | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a bitumen | |
| 610 | 1 | |a petroleum resin | |
| 610 | 1 | |a fraction of liquid pyrolysis products | |
| 610 | 1 | |a modification | |
| 610 | 1 | |a bitumenresin composition | |
| 610 | 1 | |a битум | |
| 610 | 1 | |a нефтеполимерные смолы | |
| 610 | 1 | |a продукты пиролиза | |
| 610 | 1 | |a модификации | |
| 610 | 1 | |a битумно-смоляные композиции | |
| 701 | 1 | |a Bondaletov |b V. G. |c Chemical Engineer |c Professor of Tomsk Polytechnic University, Doctor of Technical Sciences |f 1957- |g Vladimir Grigoryevich |3 (RuTPU)RU\TPU\pers\31989 |9 16049 | |
| 701 | 1 | |a Bondaletova |b L. I. |c Chemical Engineer |c Associate Professor of Tomsk Polytechnic University, Candidate of chemical sciences |f 1956- |g Lyudmila Ivanovna |3 (RuTPU)RU\TPU\pers\31991 |9 16051 | |
| 701 | 0 | |a Nguyen Van Thanh | |
| 701 | 1 | |a Bondaletova |b A. V. |g Anna Vladimirovna | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Инженерная школа природных ресурсов |b Отделение химической инженерии |3 (RuTPU)RU\TPU\col\23513 |
| 801 | 2 | |a RU |b 63413507 |c 20211224 |g RCR | |
| 856 | 4 | |u http://dx.doi.org/10.17516/1998-2836-0224 | |
| 942 | |c CF | ||