The effect of counterbody on tribological adaptation of an electron beam deposited HSS M2 steel coating in a range of sliding speeds and normal loads; Tribology International; Vol. 161

The effect of counterbody on tribological adaptation of an electron beam deposited HSS M2 steel coating in a range of sliding speeds and normal loads; Tribology International; Vol. 161

Podrobná bibliografie
Parent link:Tribology International
Vol. 161.— 2021.— [107109 , 10 p.]
Hlavní autor: Gnyusov S. F. Sergey Fedorovich
Korporativní autor: Национальный исследовательский Томский политехнический университет Инженерная школа новых производственных технологий Отделение машиностроения
Další autoři: Fedin E. A. Evgeny Aleksandrovich, Tarasov S. Yu. Sergei Yulievich
Shrnutí:Title screen
A relationship between wear behavior and structural-phase state of HSS M2 electron beam cladded coating rubbed against AISI52100 or AISIO7 counterbodies in a range of loads and speeds has been established. When rubbing the coating against the AISIO7 counterbody the wear rate increased with the normal load while coefficient of friction decreased. The effect of the counterbody on wear and friction higher speeds was related to generation of mechanically mixed layers (MMLs) composed of iron tungstate, carbide fragments and transferred metal. Steady wear rate vs. time dependence in M2/AISI O7 pair is due to higher amount of this mixed oxide.
Режим доступа: по договору с организацией-держателем ресурса
Jazyk:angličtina
Vydáno: 2021
Témata:
электронный ресурс
труды учёных ТПУ
coating
abrasive
wear
third body
покрытия
стали
электронные пучки
трение
износостойкость
On-line přístup:https://doi.org/10.1016/j.triboint.2021.107109