Low-Fired Electrotechnical Porcelain with Diopside Additives; Glass and Ceramics; Vol. 78, iss. 1-2
| Parent link: | Glass and Ceramics Vol. 78, iss. 1-2.— 2021.— [P. 18-22] |
|---|---|
| 1. autor: | |
| Korporacja: | |
| Kolejni autorzy: | , |
| Streszczenie: | Title screen The effect of diopside on the sintering temperature, structure, and properties of low-temperature electrotechnical porcelain was investigated. Diopside concentrate in the amount 12.5 wt.%, which is 10% diopside CaMgSi2O6, was introduced into a porcelain body, excluding quartz (7.2%) and decreasing the content of clay components by 5.3%. It was determined that the firing temperature was lowered by 100°C to 1220°C and the bending strength increased by 30% to 73 MPa due to reactive sintering on the interaction of diopside with the decomposition products of the clay components and anorthite and cordierite were formed. Режим доступа: по договору с организацией-держателем ресурса |
| Język: | angielski |
| Wydane: |
2021
|
| Hasła przedmiotowe: | |
| Dostęp online: | https://doi.org/10.1007/s10717-021-00358-0 |
| Format: | Elektroniczne Rozdział |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=666260 |