Spark plasma sintering of transparent YAG:Ce ceramics with LiF flux; Journal of Physics: Conference Series; Vol. 1989 : Prospects of Fundamental Sciences Development (PFSD 2021)

Spark plasma sintering of transparent YAG:Ce ceramics with LiF flux; Journal of Physics: Conference Series; Vol. 1989 : Prospects of Fundamental Sciences Development (PFSD 2021)

Detalles Bibliográficos
Parent link:Journal of Physics: Conference Series
Vol. 1989 : Prospects of Fundamental Sciences Development (PFSD 2021).— 2021.— [012008, 6 p.]
Outros autores: Paygin V. D. Vladimir Denisovich, Ilela A. E. Alfa Edison, Deulina D. E. Darjya Evgenjevna, Lyamina G. V. Galina Vladimirovna, Stepanov S. A. Sergey Aleksandrovich, Alishin T. R. Timofey Ruslanovich, Dvilis E. S. Edgar Sergeevich, Khasanov O. L. Oleg Leonidovich, Valiev D. T. Damir Talgatovich, Kalashnikov M. P. Mark Petrovich
Summary:Title screen
Transparent yttrium aluminum garnet (YAG) ceramics doped with cerium ions (Ce3+) were successfully synthesized using the spark plasma sintering (SPS) process at a temperature of 1600 °C, isothermal exposure 10 minutes, pressure 100 MPa and a heating rate 10 °C/min from a mechanical mixture of powders of yttrium, aluminum, and cerium oxides. Transmittance in the visible range for 1 mm thick samples is above 40 %; in the near infrared is above the 60 %. Vickers hardness was 15±1.05 GPa. The optimal SPS conditions have been discussed and suggested in order to obtain a good combination of density and transmittance
Idioma:inglés
Publicado: 2021
Subjects:
электронный ресурс
труды учёных ТПУ
искровое плазменное спекание
прозрачная керамика
смеси
порошки
твердость
коэффициент пропускания
Acceso en liña:http://earchive.tpu.ru/handle/11683/72803
https://doi.org/10.1088/1742-6596/1989/1/012008