Modeling the effect of the addition of alumina on structural characteristics and tensile deformation response of aluminosilicate glasses; Ceramics International; Vol. 46, iss. 13
| Источник: | Ceramics International Vol. 46, iss. 13.— 2020.— [P. 21657-21666] |
|---|---|
| Автор-организация: | |
| Другие авторы: | , , , , , |
| Примечания: | Title screen Aluminosilicate glasses, xAl2O3-(1-x)SiO2 with variable molar ratio 0 <= x <= 60%, were modeled by molecular dynamics (MD) in order to investigate the structural characteristics such as: coordination number and pair-angle distribution functions responsible for their mechanical performance. MD simulations showed that Si atoms coordinated to four O atoms are independently of the chemical composition. The number of O atoms coordinated to two decreased as the amount of Al2O3 is increased, while the opposite happened to O atoms coordinated to three. Al atoms coordinated to four O atoms were reduced as the amount of Al2O3 increases, whereas Al atoms coordinated to five O atoms were increased. Moreover, pair distribution function (PDF) study confirmed that the addition of Al2O3 causes densification of the aluminosilicate samples and, angle distribution function (ADF) corroborated PDF results and explained intermediate and long-range disorder structures of glasses. Assessment of the structural damage under uniaxial tension showed that aluminosilicate glasses are more capable of withstanding deformation without total structural failure than pure silica glasses. Режим доступа: по договору с организацией-держателем ресурса |
| Язык: | английский |
| Опубликовано: |
2020
|
| Предметы: | |
| Online-ссылка: | https://doi.org/10.1016/j.ceramint.2020.05.273 |
| Формат: | Электронный ресурс Статья |
| Запись в KOHA: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=665234 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 665234 | ||
| 005 | 20250129134047.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\36433 | ||
| 035 | |a RU\TPU\network\34059 | ||
| 090 | |a 665234 | ||
| 100 | |a 20210906d2020 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Modeling the effect of the addition of alumina on structural characteristics and tensile deformation response of aluminosilicate glasses |f T. Benitez, Rivas Murillo John Sandro, de Ligny Dominique [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 24 tit.] | ||
| 330 | |a Aluminosilicate glasses, xAl2O3-(1-x)SiO2 with variable molar ratio 0 <= x <= 60%, were modeled by molecular dynamics (MD) in order to investigate the structural characteristics such as: coordination number and pair-angle distribution functions responsible for their mechanical performance. MD simulations showed that Si atoms coordinated to four O atoms are independently of the chemical composition. The number of O atoms coordinated to two decreased as the amount of Al2O3 is increased, while the opposite happened to O atoms coordinated to three. Al atoms coordinated to four O atoms were reduced as the amount of Al2O3 increases, whereas Al atoms coordinated to five O atoms were increased. Moreover, pair distribution function (PDF) study confirmed that the addition of Al2O3 causes densification of the aluminosilicate samples and, angle distribution function (ADF) corroborated PDF results and explained intermediate and long-range disorder structures of glasses. Assessment of the structural damage under uniaxial tension showed that aluminosilicate glasses are more capable of withstanding deformation without total structural failure than pure silica glasses. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | |t Ceramics International | ||
| 463 | |t Vol. 46, iss. 13 |v [P. 21657-21666] |d 2020 | ||
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a molecular dynamics | |
| 610 | 1 | |a aluminosilicates | |
| 610 | 1 | |a glass-ceramics | |
| 610 | 1 | |a armor | |
| 610 | 1 | |a молекулярная динамика | |
| 610 | 1 | |a алюмосиликаты | |
| 610 | 1 | |a стеклокерамика | |
| 610 | 1 | |a молекулярная динамика | |
| 610 | 1 | |a алюмосиликаты | |
| 610 | 1 | |a стеклокерамика | |
| 610 | 1 | |a добавки | |
| 610 | 1 | |a оксид алюминия | |
| 610 | 1 | |a деформации | |
| 610 | 1 | |a растяжение | |
| 701 | 1 | |a Benitez |b T. |g Tobias | |
| 701 | 0 | |a Rivas Murillo John Sandro | |
| 701 | 0 | |a de Ligny Dominique | |
| 701 | 1 | |a Travitsky (Travitzky) |b N. |c specialist in the field of material science |c Professor of Tomsk Polytechnic University |f 1951- |g Nakhum |3 (RuTPU)RU\TPU\pers\42461 | |
| 701 | 0 | |a Novaes de Oliveira Antonio Pedro | |
| 701 | 1 | |a Hotza |b D. |g Dachamir | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Инженерная школа новых производственных технологий |b Отделение материаловедения |3 (RuTPU)RU\TPU\col\23508 |
| 801 | 2 | |a RU |b 63413507 |c 20210906 |g RCR | |
| 856 | 4 | |u https://doi.org/10.1016/j.ceramint.2020.05.273 | |
| 942 | |c CF | ||