Synthesis and Characterization of Nanocrystalline M-Mg-O and Carbon-Coated MgO Systems; Materials Science Forum; Vol. 917

Synthesis and Characterization of Nanocrystalline M-Mg-O and Carbon-Coated MgO Systems; Materials Science Forum; Vol. 917

Bibliographic Details
Parent link:Materials Science Forum
Vol. 917.— 2018.— [P. 157-161]
Corporate Authors: Национальный исследовательский Томский политехнический университет Исследовательская школа химических и биомедицинских технологий, Национальный исследовательский Томский политехнический университет Инженерная школа энергетики Научно-образовательный центр И. Н. Бутакова (НОЦ И. Н. Бутакова)
Other Authors: Karnaukhov T. M. Timofey Mikhaylovich, Vedyagin A. A. Aleksey Anatolievich, Mishakov I. V. Iljya Vladimirovich, Bedilo A. F. Aleksandr, Volodin A. M. Aleksandr
Summary:Title screen
Two different approaches to modify the structure and reaction ability of nanocrystalline MgO have been discussed. In the first case, a series of two-component x%MOx-MgO systems (M=Fe, Co and Ni, x=1-45 wt.%) was synthesized via sol-gel technique. Aqueous solution of inorganic salt precursor was used as a hydrolyzing agent. Samples obtained were characterized by number of physicochemical methods (differential thermal analysis, X-ray diffraction analysis, low-temperature adsorption, etc.). It was shown that presence of inorganic salt in magnesium hydroxide matrix shifts the temperature of decomposition of latter towards lower values. Structural and textural characteristics of MgO-based oxide systems were found to be strongly affected by the presence of additive and their concentration. Formation of joint phase was observed in the case of cobalt oxide only. Second way of MgO modification was represented by creating a controlled carbon coating over its surface via decomposition of C4H10 at 400 °C. The obtained x%C/MgO (x=1-10 wt.%) samples were shown to possess the improved reaction ability in destruction sorption of CF2Cl2 as well as in catalytic dehydrochlorination of 1-chlorobutane in presence of water vapors.
Режим доступа: по договору с организацией-держателем ресурса
Language:English
Published: 2018
Subjects:
электронный ресурс
труды учёных ТПУ
carbon coating
destructive sorption
halogenated hydrocarbons
nanocrystalline magnesium oxide
sol-gel technique
two-component oxides
углеродные покрытия
сорбция
углеводороды
золь-гель метод
Online Access:https://doi.org/10.4028/www.scientific.net/MSF.917.157
Format: Electronic Book Chapter
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=664771