The low-temperature specific heat of MWCNTs; Low Temperature Physics; Vol. 45, iss. 3
| Parent link: | Low Temperature Physics Vol. 45, iss. 3.— 2018.— [P. 347-354] |
|---|---|
| Erakunde egilea: | |
| Beste egile batzuk: | , , , , , , , |
| Gaia: | Title screen The specific heat of multi-walled carbon nanotubes (MWCNTs) with a low defectiveness and with a low content of inorganic impurities has been measured in the temperature range from 1.8 to 275 K by the thermal relaxation method. The elemental composition and morphology of the MWCNTs were determined using scanning electron microscopy analysis and energy dispersion x-ray spectroscopy. The MWCNTs were prepared by chemical catalytic vapor deposition and have mean diameters from 7 nm up to 18 nm and lengths in some tens of microns. MWCNTs purity is over 99.4 at.%. The mass of the samples ranged from 2-4 mg. It was found that the temperature dependence of the specific heat of the MWCNTs differs significantly from other carbon materials (graphene, bundles of SWCNTs, graphite, diamond) at low temperatures. The specific heat of MWCNTs systematically decreases with increasing diameter of the tubes at low temperatures. The character of the temperature dependence of the specific heat of the MWCNTs with different diameters demonstrates the manifestation of different dimensions from 1D to 3D, depending on the temperature regions. The crossover temperatures are about 6 and 40 K. In the vicinity of these temperatures, a hysteresis is observed. |
| Hizkuntza: | ingelesa |
| Argitaratua: |
2018
|
| Gaiak: | |
| Sarrera elektronikoa: | https://doi.org/10.1063/1.5090094 |
| Formatua: | Baliabide elektronikoa Liburu kapitulua |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=664296 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 664296 | ||
| 005 | 20250424115238.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\35480 | ||
| 035 | |a RU\TPU\network\27302 | ||
| 090 | |a 664296 | ||
| 100 | |a 20210407d2019 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a US | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a The low-temperature specific heat of MWCNTs |f V. V. Sumarokov, A. Jeowski, D. Szewczyk [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 55 tit.] | ||
| 330 | |a The specific heat of multi-walled carbon nanotubes (MWCNTs) with a low defectiveness and with a low content of inorganic impurities has been measured in the temperature range from 1.8 to 275 K by the thermal relaxation method. The elemental composition and morphology of the MWCNTs were determined using scanning electron microscopy analysis and energy dispersion x-ray spectroscopy. The MWCNTs were prepared by chemical catalytic vapor deposition and have mean diameters from 7 nm up to 18 nm and lengths in some tens of microns. MWCNTs purity is over 99.4 at.%. The mass of the samples ranged from 2-4 mg. It was found that the temperature dependence of the specific heat of the MWCNTs differs significantly from other carbon materials (graphene, bundles of SWCNTs, graphite, diamond) at low temperatures. The specific heat of MWCNTs systematically decreases with increasing diameter of the tubes at low temperatures. The character of the temperature dependence of the specific heat of the MWCNTs with different diameters demonstrates the manifestation of different dimensions from 1D to 3D, depending on the temperature regions. The crossover temperatures are about 6 and 40 K. In the vicinity of these temperatures, a hysteresis is observed. | ||
| 461 | |t Low Temperature Physics | ||
| 463 | |t Vol. 45, iss. 3 |v [P. 347-354] |d 2018 | ||
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a низкотемпературная теплоемкость | |
| 610 | 1 | |a углеродные нанотрубки | |
| 610 | 1 | |a низкие температуры | |
| 610 | 1 | |a гистерезис | |
| 610 | 1 | |a дефектность | |
| 610 | 1 | |a примеси | |
| 701 | 1 | |a Sumarokov |b V. V. |g Vladimir Victorovich | |
| 701 | 1 | |a Jeowski |b A. | |
| 701 | 1 | |a Szewczyk |b D. |g Daria | |
| 701 | 1 | |a Bagatskii |b M. I. |g Michail Ivanovich | |
| 701 | 1 | |a Ponomarev |b A. N. |g Aleksandr Nikolaevich | |
| 701 | 1 | |a Kuznetsov |b V. V. |g Vadim Vladimirovich | |
| 701 | 1 | |a Moseenkov |b S. I. |g Sergey Ivanovich | |
| 701 | 1 | |a Barabashko |b M. S. |c Physicist |c Researcher of Tomsk Polytechnic University, Doctor of physical and mathematical sciences |f 1987- |g Maksim Sergeevich |3 (RuTPU)RU\TPU\pers\38239 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Исследовательская школа физики высокоэнергетических процессов |c (2017- ) |3 (RuTPU)RU\TPU\col\23551 |
| 801 | 0 | |a RU |b 63413507 |c 20210407 |g RCR | |
| 850 | |a 63413507 | ||
| 856 | 4 | |u https://doi.org/10.1063/1.5090094 | |
| 942 | |c CF | ||