The effect of hybrid coatings based on hydrogel, biopolymer and inorganic components on the corrosion behavior of titanium bone implants; Journal of Materials Chemistry B; Vol. 7, iss. 43
| Parent link: | Journal of Materials Chemistry B Vol. 7, iss. 43.— 2019.— [P. 6778-6788] |
|---|---|
| Ente Autore: | |
| Altri autori: | , , , , , , , |
| Riassunto: | Title screen Modification of titanium (Ti) bone implant materials with hybrid organic-inorganic coatings is a novel promising approach to improve the osteoconductivity and osteointegration of implants and prevent their failure after implantation. However, in these coatings, which are mostly hydrophilic, chemically active moieties capable of releasing oxidizing ions can have a significant influence on the corrosion resistance of Ti, which is critical for the Ti implant osteointegration behavior. In this research, in order to study the dependence of the change of the corrosion behavior of Ti on the composition of the coating, Ti surfaces were modified with various coatings: organic (alginate hydrogel crosslinked with Ca2+ ions (Alg), and dextran sulfate (DS)), inorganic (porous calcium carbonate CaCO3), and composite organic-inorganic (Alg-CaCO3, DS-CaCO3). The morphology and composition of these materials before and after the corrosion experiment, performed in simulated body fluid (SBF), were followed by extensive characterization. Electrochemical impedance spectroscopy (EIS) was performed to study the corrosion behavior of the prepared materials in SBF. The characteristics obtained during the EIS measurements revealed the dependence of the variation of the corrosion resistance level on the composition of the coating. The bare Ti surface had the higher value of the total impedance compared with the modified surfaces, while the Ti surfaces modified with organic coatings demonstrated the best charge transfer resistance in comparison with the coatings containing the inorganic CaCO3 component and uncoated Ti. Режим доступа: по договору с организацией-держателем ресурса |
| Lingua: | inglese |
| Pubblicazione: |
2019
|
| Soggetti: | |
| Accesso online: | https://doi.org/10.1039/C9TB01287G |
| Natura: | Elettronico Capitolo di libro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=664069 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 664069 | ||
| 005 | 20250425142602.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\35253 | ||
| 035 | |a RU\TPU\network\34001 | ||
| 090 | |a 664069 | ||
| 100 | |a 20210326d2019 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a GB | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a The effect of hybrid coatings based on hydrogel, biopolymer and inorganic components on the corrosion behavior of titanium bone implants |f M. S. Saveleva, A. Vladesku, M. K. Kotrut [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: p. 6787-6788 (42 tit.)] | ||
| 330 | |a Modification of titanium (Ti) bone implant materials with hybrid organic-inorganic coatings is a novel promising approach to improve the osteoconductivity and osteointegration of implants and prevent their failure after implantation. However, in these coatings, which are mostly hydrophilic, chemically active moieties capable of releasing oxidizing ions can have a significant influence on the corrosion resistance of Ti, which is critical for the Ti implant osteointegration behavior. In this research, in order to study the dependence of the change of the corrosion behavior of Ti on the composition of the coating, Ti surfaces were modified with various coatings: organic (alginate hydrogel crosslinked with Ca2+ ions (Alg), and dextran sulfate (DS)), inorganic (porous calcium carbonate CaCO3), and composite organic-inorganic (Alg-CaCO3, DS-CaCO3). The morphology and composition of these materials before and after the corrosion experiment, performed in simulated body fluid (SBF), were followed by extensive characterization. Electrochemical impedance spectroscopy (EIS) was performed to study the corrosion behavior of the prepared materials in SBF. The characteristics obtained during the EIS measurements revealed the dependence of the variation of the corrosion resistance level on the composition of the coating. The bare Ti surface had the higher value of the total impedance compared with the modified surfaces, while the Ti surfaces modified with organic coatings demonstrated the best charge transfer resistance in comparison with the coatings containing the inorganic CaCO3 component and uncoated Ti. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | |t Journal of Materials Chemistry B | ||
| 463 | |t Vol. 7, iss. 43 |v [P. 6778-6788] |d 2019 | ||
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a гибридные покрытия | |
| 610 | 1 | |a гидрогели | |
| 610 | 1 | |a биополимеры | |
| 610 | 1 | |a неорганические полимеры | |
| 610 | 1 | |a коррозионное поведение | |
| 610 | 1 | |a титановые имплантаты | |
| 610 | 1 | |a костные импланты | |
| 701 | 1 | |a Saveleva |b M. S. |g Mariia | |
| 701 | 1 | |a Vladesku |b A. |c Romanian specialists in the field of biomaterials |c researcher of Tomsk Polytechnic University, candidate of biological Sciences |f 1977- |g Alina |3 (RuTPU)RU\TPU\pers\39940 | |
| 701 | 1 | |a Kotrut |b M. K. |c physicist |c physicist Professor Tomsk Polytechnic University, Ph.D. |f 1977- |g Mikhay Kosmin |3 (RuTPU)RU\TPU\pers\37467 | |
| 701 | 1 | |a Van der |b M. L. |g Meeren Louis | |
| 701 | 1 | |a Surmeneva |b M. A. |c specialist in the field of material science |c engineer-researcher of Tomsk Polytechnic University, Associate Scientist |f 1984- |g Maria Alexandrovna |3 (RuTPU)RU\TPU\pers\31894 |9 15966 | |
| 701 | 1 | |a Surmenev |b R. A. |c physicist |c Associate Professor of Tomsk Polytechnic University, Senior researcher, Candidate of physical and mathematical sciences |f 1982- |g Roman Anatolievich |3 (RuTPU)RU\TPU\pers\31885 |9 15957 | |
| 701 | 1 | |a Parakhonskiy |b B. V. |g Bogdan | |
| 701 | 1 | |a Skirtach |b A. G. |g Andre | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Инженерная школа ядерных технологий |b Научно-образовательный центр Б. П. Вейнберга |3 (RuTPU)RU\TPU\col\23561 |
| 801 | 0 | |a RU |b 63413507 |c 20210326 |g RCR | |
| 850 | |a 63413507 | ||
| 856 | 4 | |u https://doi.org/10.1039/C9TB01287G | |
| 942 | |c CF | ||