Effect of Spark Plasma Sintering Temperature on the Properties of Transparent YSZ Ceramics; Refractories and Industrial Ceramics; Vol. 60, iss. 2

Effect of Spark Plasma Sintering Temperature on the Properties of Transparent YSZ Ceramics; Refractories and Industrial Ceramics; Vol. 60, iss. 2

গ্রন্থ-পঞ্জীর বিবরন
Parent link:Refractories and Industrial Ceramics
Vol. 60, iss. 2.— 2019.— [P. 154-159]
অন্যান্য লেখক: Dvilis E. S. Edgar Sergeevich, Paygin V. D. Vladimir Denisovich, Stepanov S. A. Sergey Aleksandrovich, Khasanov O. L. Oleg Leonidovich, Valiev D. T. Damir Talgatovich, Polisadova E. F. Elena Fyodorovna, Vaganov V. A. Vitalii Andreevich, Alishin T. R. Timofey Ruslanovich, Dudina D. V. Dina Vladimirovna
সংক্ষিপ্ত:Title screen
A transparent submicron-grain sized cubic yttria-stabilized ZrO2 ceramics was obtained by spark plasma sintering in the temperature range from 1200 to 1400°C at a relatively low pre-pressing pressure (100 MPa). The produced ceramic samples have demonstrated high light transmission in the visible and near-infrared spectral regions. The paper presents elastoplastic properties and microstructure of the ceramics and discusses the relationship between the optical and elastoplastic characteristics, as well as microstructure.
Режим доступа: по договору с организацией-держателем ресурса
ভাষা:ইংরেজি
প্রকাশিত: 2019
বিষয়গুলি:
электронный ресурс
труды учёных ТПУ
yttria-stabilized zirconia
transparent ceramics
spark plasma sintering
optical properties
mechanical properties
диоксид циркония
прозрачная керамика
плазменное спекание
оптические свойства
механические свойства
অনলাইন ব্যবহার করুন:https://doi.org/10.1007/s11148-019-00327-9
বিন্যাস: বৈদ্যুতিক গ্রন্থের অধ্যায়
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=662153
বিবরন
সংক্ষিপ্ত:Title screen
A transparent submicron-grain sized cubic yttria-stabilized ZrO2 ceramics was obtained by spark plasma sintering in the temperature range from 1200 to 1400°C at a relatively low pre-pressing pressure (100 MPa). The produced ceramic samples have demonstrated high light transmission in the visible and near-infrared spectral regions. The paper presents elastoplastic properties and microstructure of the ceramics and discusses the relationship between the optical and elastoplastic characteristics, as well as microstructure.