Ion modification of alumina ceramics; Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms; Vol. 464
| Parent link: | Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms Vol. 464.— 2020.— [Р. 89-94] |
|---|---|
| Tác giả của công ty: | |
| Tác giả khác: | , , , , |
| Tóm tắt: | Title screen The patterns of depth microhardness, nanohardness and modulus of elasticity of alumina ceramics were investigated by microindentation and nanoindentation methods after treatment with a beam of ions of the composition: carbon ions (C+, Cn+) and protons (H+) in a ratio of 85%/15%. The accelerating voltage was 180 keV. The experiments were performed at pulse energy density (W) of 0.3, 1 and 1.5 J/cm2. It is shown that ion treatment increases the strength of the surface layers of ceramics at depth that exceeds the penetration depth of accelerated ions by an order of magnitude or more. That is, there is a long-range effect characteristic of the ion treatment of metals and alloys. The analysis of the processes of energy release and structural changes in the surface layers shows that melting and recrystallization of the thin surface layer of ceramics observed in ion treatment are not the determining factors that change the strength properties of ceramics under these layers. It is shown that hardening of these layers occurs by the shock-wave mechanism initiated by local overheating of the surface layers of ceramics by intense pulsed ion beam. Режим доступа: по договору с организацией-держателем ресурса |
| Ngôn ngữ: | Tiếng Anh |
| Được phát hành: |
2020
|
| Những chủ đề: | |
| Truy cập trực tuyến: | https://doi.org/10.1016/j.nimb.2019.12.013 |
| Định dạng: | MixedMaterials Điện tử Chương của sách |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=661715 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 661715 | ||
| 005 | 20250417134318.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\32515 | ||
| 090 | |a 661715 | ||
| 100 | |a 20200206d2020 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a NL | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Ion modification of alumina ceramics |f S. A. Gyngazov (Ghyngazov) [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 76 tit.] | ||
| 330 | |a The patterns of depth microhardness, nanohardness and modulus of elasticity of alumina ceramics were investigated by microindentation and nanoindentation methods after treatment with a beam of ions of the composition: carbon ions (C+, Cn+) and protons (H+) in a ratio of 85%/15%. The accelerating voltage was 180 keV. The experiments were performed at pulse energy density (W) of 0.3, 1 and 1.5 J/cm2. It is shown that ion treatment increases the strength of the surface layers of ceramics at depth that exceeds the penetration depth of accelerated ions by an order of magnitude or more. That is, there is a long-range effect characteristic of the ion treatment of metals and alloys. The analysis of the processes of energy release and structural changes in the surface layers shows that melting and recrystallization of the thin surface layer of ceramics observed in ion treatment are not the determining factors that change the strength properties of ceramics under these layers. It is shown that hardening of these layers occurs by the shock-wave mechanism initiated by local overheating of the surface layers of ceramics by intense pulsed ion beam. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | |t Nuclear Instruments and Methods in Physics Research Section B: Beam Interactions with Materials and Atoms | ||
| 463 | |t Vol. 464 |v [Р. 89-94] |d 2020 | ||
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a ионная модификация | |
| 610 | 1 | |a глиноземное производство | |
| 610 | 1 | |a керамика | |
| 701 | 1 | |a Gyngazov (Ghyngazov) |b S. A. |c specialist in the field of electronics |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1958- |g Sergey Anatolievich |3 (RuTPU)RU\TPU\pers\33279 |9 17024 | |
| 701 | 1 | |a Kostenko |b V. |c specialist in the field of electrical engineering |c laboratory assistant researcher of Tomsk Polytechnic University |f 1994- |g Valeriya |3 (RuTPU)RU\TPU\pers\42079 | |
| 701 | 1 | |a Shevelev |b S. A. |c specialist in the field of heat and power engineering |c senior lecturer of Tomsk Polytechnic University |f 1983- |g Sergey Anatolievich |3 (RuTPU)RU\TPU\pers\36037 |9 19174 | |
| 701 | 1 | |a Lysenko |b E. N. |c Specialist in the field of electrical engineering |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1972- |g Elena Nikolaevna |3 (RuTPU)RU\TPU\pers\32050 |9 16097 | |
| 701 | 1 | |a Surzhikov |b A. P. |c physicist |c Professor of Tomsk Polytechnic University, doctor of physical and mathematical sciences (DSc) |f 1951- |g Anatoly Petrovich |3 (RuTPU)RU\TPU\pers\30237 |9 14617 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Институт неразрушающего контроля |b Проблемная научно-исследовательская лаборатория электроники, диэлектриков и полупроводников |3 (RuTPU)RU\TPU\col\19033 |
| 801 | 2 | |a RU |b 63413507 |c 20200206 |g RCR | |
| 850 | |a 63413507 | ||
| 856 | 4 | |u https://doi.org/10.1016/j.nimb.2019.12.013 | |
| 942 | |c CF | ||