Temperature Dependence of Inelastic Recoverable Strain and Degree of Shape Recovery in Coarse-Grained Samples of Ti[49.3]Ni[50.7] (at %) in the Absence of Plastic Deformation; AIP Conference Proceedings; Vol. 2167 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2019 (AMHS'19)
| Parent link: | AIP Conference Proceedings Vol. 2167 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2019 (AMHS'19).— 2019.— [020399, 4 p.] |
|---|---|
| Údar corparáideach: | |
| Rannpháirtithe: | , , , , |
| Achoimre: | Title screen The results of studies of inelastic reversible strains and degree of shape recovery in samples of Ti[49.3]Ni[50.7] (at %) alloy depending on the test temperature and phase state were presented. It is shown that high values of inelastic reversible strain in the absence of plastic deformation were observed in samples with the initial martensite structure B19′, two-phase structure В2 + В19′, and with the structure of high-temperature B2 phase. The influence of correlation of the yield stress and martensite shear stress on the manifestation of reversible inelastic strains and the development of plastic deformation was discussed. Режим доступа: по договору с организацией-держателем ресурса |
| Teanga: | Béarla |
| Foilsithe / Cruthaithe: |
2019
|
| Ábhair: | |
| Rochtain ar líne: | https://doi.org/10.1063/1.5132266 |
| Formáid: | Leictreonach Caibidil leabhair |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=661560 |
| Achoimre: | Title screen The results of studies of inelastic reversible strains and degree of shape recovery in samples of Ti[49.3]Ni[50.7] (at %) alloy depending on the test temperature and phase state were presented. It is shown that high values of inelastic reversible strain in the absence of plastic deformation were observed in samples with the initial martensite structure B19′, two-phase structure В2 + В19′, and with the structure of high-temperature B2 phase. The influence of correlation of the yield stress and martensite shear stress on the manifestation of reversible inelastic strains and the development of plastic deformation was discussed. Режим доступа: по договору с организацией-держателем ресурса |
|---|---|
| DOI: | 10.1063/1.5132266 |