Metal Powder Composite Based on 316L Stainless Steel Bimodal Powder; AIP Conference Proceedings; Vol. 2167 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2019 (AMHS'19)
| Parent link: | AIP Conference Proceedings Vol. 2167 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2019 (AMHS'19).— 2019.— [020366, 4 p.] |
|---|---|
| Ente Autore: | |
| Altri autori: | , , , , , , |
| Riassunto: | Title screen Metal powder composites for Powder injection molding (PIM) technology have been investigated. 316L stainless steel bimodal powder, obtained by electric explosion of the wire and multicomponent binder comprising PMMA, PE-LD and Viscowax were used to obtain feedstocks. The effect of PMMA content in the binder on the properties of feedstocks and sintered parts has been studied. As the PMMA content increases, the molding temperature of the parts rises from 140 to 200°C, the strength of the "green" and "brow" parts increases as well. The optimal PMMA content in the binder has been found to be 15-20 vol %. "Brown" samples sintered in vacuum at 1300°C exhibit shrinkage up to 23% and the samples density reaches 0.98 TD. Samples of feedstocks were characterized by TEM, SEM, DSC-TG methods. Режим доступа: по договору с организацией-держателем ресурса |
| Lingua: | inglese |
| Pubblicazione: |
2019
|
| Soggetti: | |
| Accesso online: | https://doi.org/10.1063/1.5132233 |
| Natura: | Elettronico Capitolo di libro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=661555 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 661555 | ||
| 005 | 20260202144831.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\32184 | ||
| 035 | |a RU\TPU\network\32183 | ||
| 090 | |a 661555 | ||
| 100 | |a 20200113d2019 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 135 | |a drgn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Metal Powder Composite Based on 316L Stainless Steel Bimodal Powder |f N. E. Toropkov [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 3 tit.] | ||
| 330 | |a Metal powder composites for Powder injection molding (PIM) technology have been investigated. 316L stainless steel bimodal powder, obtained by electric explosion of the wire and multicomponent binder comprising PMMA, PE-LD and Viscowax were used to obtain feedstocks. The effect of PMMA content in the binder on the properties of feedstocks and sintered parts has been studied. As the PMMA content increases, the molding temperature of the parts rises from 140 to 200°C, the strength of the "green" and "brow" parts increases as well. The optimal PMMA content in the binder has been found to be 15-20 vol %. "Brown" samples sintered in vacuum at 1300°C exhibit shrinkage up to 23% and the samples density reaches 0.98 TD. Samples of feedstocks were characterized by TEM, SEM, DSC-TG methods. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\network\4816 |t AIP Conference Proceedings | |
| 463 | 1 | |0 (RuTPU)RU\TPU\network\31884 |t Vol. 2167 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2019 (AMHS'19) |o Proceedings of the International Conference, 1–5 October 2019, Tomsk, Russia |f National Research Tomsk Polytechnic University (TPU) ; Institute of Strength Physics and Materials Science SB RAS (Russia) ; eds. V. E. Panin ; S. G. Psakhie ; V. M. Fomin |v [020366, 4 p.] |d 2019 | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a композитные порошки | |
| 610 | 1 | |a металлические порошки | |
| 610 | 1 | |a нержавеющие стали | |
| 610 | 1 | |a литье | |
| 610 | 1 | |a электрический взрыв | |
| 610 | 1 | |a связующие | |
| 610 | 1 | |a спеченные детали | |
| 701 | 1 | |a Toropkov |b N. E. |c Chemical engineer |c Engineer of Tomsk Polytechnic University |f 1992- |g Nikita Evgenievich |3 (RuTPU)RU\TPU\pers\45800 | |
| 701 | 1 | |a Glazkova |b E. |g Elena | |
| 701 | 1 | |a Rodkevich |b N. |g Nikolay | |
| 701 | 1 | |a Pervikov |b A. |g Aleksandr | |
| 701 | 1 | |a Lerner |b M. I. |c specialist in the field of mechanical engineering |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1956- |g Marat Izrailyevich |3 (RuTPU)RU\TPU\pers\31423 | |
| 701 | 1 | |a Muzhetskaya |b S. |g Svetlana | |
| 701 | 1 | |a Gyngazov (Ghyngazov) |b S. A. |c specialist in the field of electronics |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1958- |g Sergey Anatolievich |3 (RuTPU)RU\TPU\pers\33279 |9 17024 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Институт неразрушающего контроля |b Проблемная научно-исследовательская лаборатория электроники, диэлектриков и полупроводников |3 (RuTPU)RU\TPU\col\19033 |
| 801 | 2 | |a RU |b 63413507 |c 20200113 |g RCR | |
| 856 | 4 | |u https://doi.org/10.1063/1.5132233 | |
| 942 | |c CF | ||