| Tóm tắt: | Title screen The formation of strain inhomogeneity of zirconia ceramics have been studied during Brazilian test using a digital image correlation method. It was shown that with increasing load the deformation along the longitudinal axis was about 0.3%, and along the transverse axis less or equal to 0.12 %.The component of strain [epsilon][хх] and [epsilon][yy] has a non-uniform distributions on the sample surface and deformation of zirconia proceeds macroscopically localized. Coherently diffracting domains of the tetragonal phase and lattice microdistortion changes compared with the initial state after sintering and differ on different fracture fragments of the sample after its fracture. It was found that microstresses measured on different surfaces of fracture fragments of sample change in the range of 245-320 MPa, in accordance with the arising inhomogeneity of deformation. Strain localization correlates with inhomogeneity of the microstresses in the material during deformation. Режим доступа: по договору с организацией-держателем ресурса |
| Ngôn ngữ: | Tiếng Anh |
| Được phát hành: |
2019
|
| Những chủ đề: | |
| Truy cập trực tuyến: | https://doi.org/10.1063/1.5132169 |
| Định dạng: | Điện tử Chương của sách |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=661543 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 661543 | ||
| 005 | 20260203140854.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\32172 | ||
| 035 | |a RU\TPU\network\32164 | ||
| 090 | |a 661543 | ||
| 100 | |a 20200113d2019 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Investigation of the Strain Inhomogeneity of ZrO[2]-(Y[2]O[3]) during Brazilian Test |f T. Yu. Sablina [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 12 tit.] | ||
| 330 | |a The formation of strain inhomogeneity of zirconia ceramics have been studied during Brazilian test using a digital image correlation method. It was shown that with increasing load the deformation along the longitudinal axis was about 0.3%, and along the transverse axis less or equal to 0.12 %.The component of strain [epsilon][хх] and [epsilon][yy] has a non-uniform distributions on the sample surface and deformation of zirconia proceeds macroscopically localized. Coherently diffracting domains of the tetragonal phase and lattice microdistortion changes compared with the initial state after sintering and differ on different fracture fragments of the sample after its fracture. It was found that microstresses measured on different surfaces of fracture fragments of sample change in the range of 245-320 MPa, in accordance with the arising inhomogeneity of deformation. Strain localization correlates with inhomogeneity of the microstresses in the material during deformation. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\network\4816 |t AIP Conference Proceedings | |
| 463 | 1 | |0 (RuTPU)RU\TPU\network\31884 |t Vol. 2167 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2019 (AMHS'19) |o Proceedings of the International Conference, 1–5 October 2019, Tomsk, Russia |f National Research Tomsk Polytechnic University (TPU) ; Institute of Strength Physics and Materials Science SB RAS (Russia) ; eds. V. E. Panin ; S. G. Psakhie ; V. M. Fomin |v [020302, 5 p.] |d 2019 | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a неоднородности | |
| 610 | 1 | |a циркониевая керамика | |
| 610 | 1 | |a цифровая коррекция | |
| 610 | 1 | |a изображения | |
| 610 | 1 | |a нагрузки | |
| 610 | 1 | |a поверхности | |
| 610 | 1 | |a цирконий | |
| 610 | 1 | |a неоднородности | |
| 610 | 1 | |a разрушения | |
| 701 | 1 | |a Sablina |b T. Yu. | |
| 701 | 1 | |a Sevostyanova |b I. N. | |
| 701 | 1 | |a Gorbatenko |b V. V. | |
| 701 | 1 | |a Ryzhova |b L. N. | |
| 701 | 1 | |a Molchunova |b L. M. | |
| 701 | 1 | |a Kulkov |b S. N. |c specialist in the field of material science |c Professor of Tomsk Polytechnic University, Doctor of physical and mathematical sciences |f 1952- |g Sergey Nikolaevich |3 (RuTPU)RU\TPU\pers\31428 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Инженерная школа новых производственных технологий |b Отделение материаловедения |3 (RuTPU)RU\TPU\col\23508 |
| 801 | 2 | |a RU |b 63413507 |c 20200113 |g RCR | |
| 856 | 4 | |u https://doi.org/10.1063/1.5132169 | |
| 942 | |c CF | ||