Deformation and Fracture of Hypereutectic Silumin Samples with a Surface Modified with an Intense Pulsed Electron Beam
| Parent link: | AIP Conference Proceedings Vol. 2167 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2019 (AMHS'19).— 2019.— [020160, 5 p.] |
|---|---|
| Autor corporatiu: | |
| Altres autors: | , , , , , , , , , , |
| Sumari: | Title screen Development of structural light-weight materials with necessary performance characteristics is an important task as they are used in mechanical engineering, aviation and space. It is known that macroproperties of a material depend on the structural-phase state at micro- and meso- level. One of the methods of transformation of the material structure is irradiation of the surface with an intense pulsed electron beam. The purpose of the paper is the analysis of the laws governing formation of a destruction surface structure of hypereutectic silumin AK10M2N in the as-cast state and in the state after exposure to a pulsed electron beam. Deformation of silumin samples was carried out using the strain to failure method. Electron beam irradiation was carried out in the high-speed melting mode of the surface layer of samples prepared for tensile testing. As a result of the studies, it has been found that irradiation leads to formation of multiphase structure with micro- and nanoscale inclusions in the treated surface layer with a thickness up to 70 [mu]m. An increase in strength (in 2 times) and plastic (in 1.8 times) properties of silumin irradiated with an electron beam has been revealed. Режим доступа: по договору с организацией-держателем ресурса |
| Idioma: | anglès |
| Publicat: |
2019
|
| Matèries: | |
| Accés en línia: | https://doi.org/10.1063/1.5132027 |
| Format: | Electrònic Capítol de llibre |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=661503 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 661503 | ||
| 005 | 20260209133547.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\32116 | ||
| 035 | |a RU\TPU\network\32115 | ||
| 090 | |a 661503 | ||
| 100 | |a 20191230d2019 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Deformation and Fracture of Hypereutectic Silumin Samples with a Surface Modified with an Intense Pulsed Electron Beam |f A. Klopotov [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 27 tit.] | ||
| 330 | |a Development of structural light-weight materials with necessary performance characteristics is an important task as they are used in mechanical engineering, aviation and space. It is known that macroproperties of a material depend on the structural-phase state at micro- and meso- level. One of the methods of transformation of the material structure is irradiation of the surface with an intense pulsed electron beam. The purpose of the paper is the analysis of the laws governing formation of a destruction surface structure of hypereutectic silumin AK10M2N in the as-cast state and in the state after exposure to a pulsed electron beam. Deformation of silumin samples was carried out using the strain to failure method. Electron beam irradiation was carried out in the high-speed melting mode of the surface layer of samples prepared for tensile testing. As a result of the studies, it has been found that irradiation leads to formation of multiphase structure with micro- and nanoscale inclusions in the treated surface layer with a thickness up to 70 [mu]m. An increase in strength (in 2 times) and plastic (in 1.8 times) properties of silumin irradiated with an electron beam has been revealed. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\network\4816 |t AIP Conference Proceedings | |
| 463 | 1 | |0 (RuTPU)RU\TPU\network\31884 |t Vol. 2167 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2019 (AMHS'19) |o Proceedings of the International Conference, 1–5 October 2019, Tomsk, Russia |f National Research Tomsk Polytechnic University (TPU) ; Institute of Strength Physics and Materials Science SB RAS (Russia) ; eds. V. E. Panin ; S. G. Psakhie ; V. M. Fomin |v [020160, 5 p.] |d 2019 | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a деформации | |
| 610 | 1 | |a разрушения | |
| 610 | 1 | |a силумины | |
| 610 | 1 | |a поверхности | |
| 610 | 1 | |a электронные пучки | |
| 610 | 1 | |a конструкционные материалы | |
| 610 | 1 | |a эксплуатационные характеристики | |
| 610 | 1 | |a структура | |
| 610 | 1 | |a поверхностные слои | |
| 701 | 1 | |a Klopotov |b A. |g Anatoliy | |
| 701 | 1 | |a Ivanov |b Yu. F. |c physicist |c Professor of Tomsk Polytechnic University, Doctor of physical and mathematical sciences |f 1955- |g Yuriy Fedorovich |3 (RuTPU)RU\TPU\pers\33559 | |
| 701 | 1 | |a Zagulyaev |b D. |g Dmitriy | |
| 701 | 1 | |a Ustinov |b A. |g Artyom | |
| 701 | 1 | |a Petrikova |b E. |g Elizaveta | |
| 701 | 1 | |a Teresov |b A. |g Anton | |
| 701 | 1 | |a Rygina |b M. |g Mariya | |
| 701 | 1 | |a Abzaev |b Yu. |g Yuriy | |
| 701 | 1 | |a Potekaev |b A. |g Aleksandr | |
| 701 | 1 | |a Volokitin |b O. |g Oleg | |
| 701 | 1 | |a Vlasov |b Yu. |g Yuriy | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Исследовательская школа химических и биомедицинских технологий |b Научно-исследовательский центр "Физическое материаловедение и композитные материалы" |3 (RuTPU)RU\TPU\col\24957 |
| 801 | 2 | |a RU |b 63413507 |c 20201029 |g RCR | |
| 856 | 4 | |u https://doi.org/10.1063/1.5132027 | |
| 942 | |c CF | ||