Alumina-based composites reinforced with single-walled carbon nanotubes; IOP Conference Series: Materials Science and Engineering; Vol. 511 : Perspective Materials of Constructional and Medical Purpose
| Parent link: | IOP Conference Series: Materials Science and Engineering Vol. 511 : Perspective Materials of Constructional and Medical Purpose.— 2019.— [012001, 6 p.] |
|---|---|
| Hovedforfatter: | |
| Institution som forfatter: | |
| Andre forfattere: | |
| Summary: | Title screen Monolithic Al[2]O[3] ceramics and Al[2]O[3] - 3 vol% single-walled carbon nanotubes (SWCNTs) composites were prepared by spark plasma sintering. The influence of SWCNTs and sintering temperature on sintering behavior and mechanical properties were investigated. Nanotubes were relatively homogeneously distributed in the composite powder, although some agglomerates/bundles existed. It was found that SWCNTs addition retards slightly the sinterability of alumina by nanotubes hindering of particle rearrangement. The average microhardness of the composites was lower than that of Al[2]O[3] ceramics, but there were also high microhardness values of composites (20.41 GPa). The reduction in microhardness is explained in this paper. The average values of the fracture toughness (4.94 MPa·m{1/2}) from the composite sintered at 1500 °C were approximately 6 % and 12 % higher than those from the Al[2]O[3] ceramics sintered at 1500 °C and 1600 °C, respectively. In addition, the analysis of the phase composition and the parameters of the crystal structure of the samples were made. |
| Sprog: | engelsk |
| Udgivet: |
2019
|
| Fag: | |
| Online adgang: | http://dx.doi.org/10.1088/1757-899X/511/1/012001 http://earchive.tpu.ru/handle/11683/55431 |
| Format: | Electronisk Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=660529 |
MARC
| LEADER | 00000nla2a2200000 4500 | ||
|---|---|---|---|
| 001 | 660529 | ||
| 005 | 20231101135130.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\30012 | ||
| 035 | |a RU\TPU\network\28328 | ||
| 090 | |a 660529 | ||
| 100 | |a 20190724d2019 k y0engy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a GB | ||
| 105 | |a y z 100zy | ||
| 135 | |a vrcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Alumina-based composites reinforced with single-walled carbon nanotubes |f A. A. Leonov, E. V. Abdulmenova | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 37 tit.] | ||
| 330 | |a Monolithic Al[2]O[3] ceramics and Al[2]O[3] - 3 vol% single-walled carbon nanotubes (SWCNTs) composites were prepared by spark plasma sintering. The influence of SWCNTs and sintering temperature on sintering behavior and mechanical properties were investigated. Nanotubes were relatively homogeneously distributed in the composite powder, although some agglomerates/bundles existed. It was found that SWCNTs addition retards slightly the sinterability of alumina by nanotubes hindering of particle rearrangement. The average microhardness of the composites was lower than that of Al[2]O[3] ceramics, but there were also high microhardness values of composites (20.41 GPa). The reduction in microhardness is explained in this paper. The average values of the fracture toughness (4.94 MPa·m{1/2}) from the composite sintered at 1500 °C were approximately 6 % and 12 % higher than those from the Al[2]O[3] ceramics sintered at 1500 °C and 1600 °C, respectively. In addition, the analysis of the phase composition and the parameters of the crystal structure of the samples were made. | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\network\2008 |t IOP Conference Series: Materials Science and Engineering | |
| 463 | 1 | |0 (RuTPU)RU\TPU\network\29838 |t Vol. 511 : Perspective Materials of Constructional and Medical Purpose |o International Scientific and Technical Youth Conference, 26–30 November 2018, Tomsk, Russian Federation |o [proceedings] |v [012001, 6 p.] |d 2019 | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a композиты | |
| 610 | 1 | |a оксид алюминия | |
| 610 | 1 | |a армирование | |
| 610 | 1 | |a углеродные нанотрубки | |
| 610 | 1 | |a спекание | |
| 610 | 1 | |a микротвердость | |
| 610 | 1 | |a фазовый состав | |
| 610 | 1 | |a кристаллические структуры | |
| 700 | 1 | |a Leonov |b A. A. |c Specialist in the field of material science |c Specialist in educational and methodical work of Tomsk Polytechnic University |f 1991- |g Andrey Andreevich |2 stltpush |3 (RuTPU)RU\TPU\pers\38521 | |
| 701 | 1 | |a Abdulmenova |b E. V. |c Specialist in the field of material science |c Engineer of Tomsk Polytechnic University |f 1993- |g Ekaterina Vladimirovna |2 stltpush |3 (RuTPU)RU\TPU\pers\45719 | |
| 712 | 0 | 2 | |a National Research Tomsk Polytechnic University (TPU) |2 stltpush |3 (RuTPU)RU\TPU\col\18773 |
| 801 | 1 | |a RU |b 63413507 |c 20150101 |g RCR | |
| 801 | 2 | |a RU |b 63413507 |c 20191226 |g RCR | |
| 856 | 4 | |u http://dx.doi.org/10.1088/1757-899X/511/1/012001 | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/55431 | |
| 942 | |c CF | ||