Structure and defects evolution at temperature and activation treatments of the TiCr2 intermetallic compound of Laves phase C36-type; International Journal of Hydrogen Energy; Vol. 44, iss. 21
| Parent link: | International Journal of Hydrogen Energy Vol. 44, iss. 21.— 2019.— [P. 10732-10743] |
|---|---|
| Korporativna značnica: | |
| Drugi avtorji: | , , , , |
| Izvleček: | Title screen In this work, microstructure and defect evolution at a temperature and activation treatment of the TiCr2 intermetallic compound of Laves phase C36-type synthesized in the abnormal glow discharge plasma were investigated. The crystalline structure of the C36TiCr2 powder crushed by hydrogenation-dehydrogenation (HD) method is characterized by the following lattice parameters: a = 4.932 Е and c = 16.059 Е. The dilatation of the crystal lattice under the hydrogenation at the HD crushing process leads to the formation of partial dislocations. For the first time ever the experimental value of the positron lifetime of the synthesized compound of the C36TiCr2 Laves phase, this amounted to (141 ± 2) ps, established by the positron spectroscopy. The optimal activation parameters of the HD-crushing C36TiCr2 powder were established: the temperature should be in the range from 450 to 500 °C, the exposure time in a hydrogen atmosphere at a pressure of (1–8) atm. must be at least 10 min. Режим доступа: по договору с организацией-держателем ресурса |
| Jezik: | angleščina |
| Izdano: |
2019
|
| Teme: | |
| Online dostop: | https://doi.org/10.1016/j.ijhydene.2019.02.154 |
| Format: | MixedMaterials Elektronski Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=660308 |