Parameters of Iron and Aluminum Nano- and Micropowder Activity upon Oxidation in Air under Microwave Irradiation; Journal of Applied Mechanics and Technical Physics; Vol. 63, iss. 9
| Parent link: | Journal of Applied Mechanics and Technical Physics Vol. 63, iss. 9.— 2018.— [P. 1223-1227] |
|---|---|
| Համատեղ հեղինակներ: | , |
| Այլ հեղինակներ: | , , , |
| Ամփոփում: | Title screen Iron nanopowders and iron and aluminum micropowders exposed to microwave radiation with a frequency of 9.4 GHz and a power density of 80 W/cm2 at a pulse repetition rate of 400 Hz have been investigated. According to the results of differential thermal analysis, the microwave radiation caused nonmonotonic changes in the thermal properties of the A1 and Fe powders. After irradiation of the iron nanopowder, the temperature of the onset of its oxidation increased from 150.01 to 158.75°C; in the case of the micropowder, the temperature nonmonotonically changed from 150.00 to 275.38°C. The specific heat of oxidation of the Fe nanopowder increased by 17.3% at maximum, while in the Fe micropowder the maximum attained increase was 13%. For the Al micropowder, the maximum increase in the specific heat of oxidation was found to be 59.7%. Microwave irradiation leads to the formation of electron avalanches, which reduce metal ions in their oxides. At the same time, at certain irradiation doses the generated electron flows oxidize the reduced metals, which is reflected in the nonmonotonic variation in the properties of a material. The increase in the specific heat of oxidation is related to the participation of energy-saturated states of the metals in the oxidation processes. Режим доступа: по договору с организацией-держателем ресурса |
| Լեզու: | անգլերեն |
| Հրապարակվել է: |
2018
|
| Խորագրեր: | |
| Առցանց հասանելիություն: | https://doi.org/10.1134/S1063784218080133 |
| Ձևաչափ: | Էլեկտրոնային Գրքի գլուխ |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=660136 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 660136 | ||
| 005 | 20250331142340.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\29086 | ||
| 035 | |a RU\TPU\network\28572 | ||
| 090 | |a 660136 | ||
| 100 | |a 20190426d2018 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a US | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Parameters of Iron and Aluminum Nano- and Micropowder Activity upon Oxidation in Air under Microwave Irradiation |f A. V. Mostovshchikov [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 21 tit.] | ||
| 330 | |a Iron nanopowders and iron and aluminum micropowders exposed to microwave radiation with a frequency of 9.4 GHz and a power density of 80 W/cm2 at a pulse repetition rate of 400 Hz have been investigated. According to the results of differential thermal analysis, the microwave radiation caused nonmonotonic changes in the thermal properties of the A1 and Fe powders. After irradiation of the iron nanopowder, the temperature of the onset of its oxidation increased from 150.01 to 158.75°C; in the case of the micropowder, the temperature nonmonotonically changed from 150.00 to 275.38°C. The specific heat of oxidation of the Fe nanopowder increased by 17.3% at maximum, while in the Fe micropowder the maximum attained increase was 13%. For the Al micropowder, the maximum increase in the specific heat of oxidation was found to be 59.7%. Microwave irradiation leads to the formation of electron avalanches, which reduce metal ions in their oxides. At the same time, at certain irradiation doses the generated electron flows oxidize the reduced metals, which is reflected in the nonmonotonic variation in the properties of a material. The increase in the specific heat of oxidation is related to the participation of energy-saturated states of the metals in the oxidation processes. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | |t Journal of Applied Mechanics and Technical Physics | ||
| 463 | |t Vol. 63, iss. 9 |v [P. 1223-1227] |d 2018 | ||
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a нанопорошки | |
| 610 | 1 | |a железо | |
| 610 | 1 | |a алюминий | |
| 610 | 1 | |a окисление в воздухе | |
| 610 | 1 | |a микроволновое облучение | |
| 701 | 1 | |a Mostovshchikov |b A. V. |c Chemist |c Senior Researcher, Professor of Tomsk Polytechnic University, Doctor of Technical Sciences |f 1989- |g Andrey Vladimirovich |3 (RuTPU)RU\TPU\pers\31091 |9 15320 | |
| 701 | 1 | |a Ilyin |b A. P. |c chemist |c Professor of Tomsk Polytechnic University, Doctor of physical and mathematical sciences |f 1949- |g Aleksandr Petrovich |3 (RuTPU)RU\TPU\pers\33060 |9 16894 | |
| 701 | 1 | |a Chumerin |b P. Yu. |c physicist |c Senior researcher of Tomsk Polytechnic University, Doctor of physical and mathematical science |f 1958- |g Pavel Yurievich |3 (RuTPU)RU\TPU\pers\32716 | |
| 701 | 1 | |a Yushkov |b Y. G. |c electrophysicist |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1937- |g Yuri Georgievich |3 (RuTPU)RU\TPU\pers\25936 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Инженерная школа ядерных технологий |b Научно-исследовательская лаборатория СВЧ-технологии |3 (RuTPU)RU\TPU\col\23457 |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Школа базовой инженерной подготовки |b Отделение естественных наук |3 (RuTPU)RU\TPU\col\23562 |
| 801 | 2 | |a RU |b 63413507 |c 20190426 |g RCR | |
| 856 | 4 | |u https://doi.org/10.1134/S1063784218080133 | |
| 942 | |c CF | ||