Thermal Stability of Structure and Properties of the Surface Layer of Instrumental Steel Alloyed with Zirconium and Silicon Atoms under the Action of Compression Plasma Flows; Inorganic Materials: Applied Research; Vol. 9, iss. 5

Thermal Stability of Structure and Properties of the Surface Layer of Instrumental Steel Alloyed with Zirconium and Silicon Atoms under the Action of Compression Plasma Flows; Inorganic Materials: Applied Research; Vol. 9, iss. 5

Bibliographische Detailangaben
Parent link:Inorganic Materials: Applied Research
Vol. 9, iss. 5.— 2018.— [P. 965-972]
Körperschaft: Национальный исследовательский Томский политехнический университет Исследовательская школа физики высокоэнергетических процессов
Weitere Verfasser: Cherenda N. N. Nikolay Nikolaevich, Uglov V. V. Vladimir Vasilievich, Gusakova S. V. Svetlana Valerjevna, Astashinsky V. M. Valentin Mironovich, Kuzmitsky A. M. Anton Mikhaylovich
Zusammenfassung:Title screen
The phase and elemental composition and microhardness of instrumental steel U9 with zirconium and silicon coatings subjected to compression plasma flows and air thermal annealing are investigated. It is found that plasma impact leads to the formation of a surface layer with the thickness of up to ~8.5 m alloyed with zirconium and silicon atoms and containing Fe2Zr intermetallic. Formation on the surface of the oxide ?-ZrO2 and carbonitride Zr(C, N) as a result of interaction with the residual atmosphere of the vacuum chamber is found. Change in the phase composition and dispersion of the structure leads to a twofold increase in microhardness. The alloyed layer retains the stability of the structure and phase composition (excluding polymorphic transition in ZrO2) up to 400°C. Annealing at 600°C leads to the internal oxidation accompanied by formation of a surface iron oxide scale and penetration of the oxygen atoms to the whole depth. The increase in the annealing temperature leads to the decrease in microhardness throughout the alloyed layer.
Режим доступа: по договору с организацией-держателем ресурса
Sprache:Englisch
Veröffentlicht: 2018
Schlagworte:
электронный ресурс
труды учёных ТПУ
steel
compression plasma flows
phase composition
corrosion resistance
microhardness
сталь
плазменные потоки
фазовый состав
коррозионная стойкость
микротвердость
Online-Zugang:https://doi.org/10.1134/S2075113318050052
Format: Elektronisch Buchkapitel
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=660083

Ähnliche Einträge

Ähnliche Einträge