Optical excitation thermography for twill/plain weaves and stitched fabric dry carbon fibre preform inspection
| Parent link: | Composites Part A: Applied Science and Manufacturing Vol. 107.— 2018.— [P. 282-293] |
|---|---|
| Corporate Author: | |
| Other Authors: | , , , , , , |
| Summary: | Title screen Carbon fibres have become the natural choice as reinforcements for polymer composite materials (PMCs). The non-destructive inspection of dry carbon fibre preforms has the potential to increase the reproducibility and reduce the cost of PMC manufacturing, by identifying defects in dry multilayer preforms prior to resin injection. However, use of optical excitation thermography for inspecting dry carbon fibre preforms that constitute the structural reinforcement precursor in the manufacturing of PMCs is poorly documented in the open literature. In this work, optical excitation thermography was used for inspecting six dry multilayer carbon fibre preforms featuring different textile structures, thicknesses and defects, for the first time. Advanced image processing techniques were used in processing the thermographic data for comparative purposes. In particular, partial least square thermography, as a recently proposed technique, was studied in detail. Finally, the performance of different thermography techniques was analysed in terms of: (1) summarizing the capabilities of image diagnosis/processing techniques by signal-to-noise ratio analysis, and (2) identifying the monitoring modalities most suitable to industrial manufacturing. Режим доступа: по договору с организацией-держателем ресурса |
| Language: | English |
| Published: |
2018
|
| Subjects: | |
| Online Access: | https://doi.org/10.1016/j.compositesa.2018.01.006 |
| Format: | Electronic Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=659686 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 659686 | ||
| 005 | 20250326150105.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\28413 | ||
| 035 | |a RU\TPU\network\27422 | ||
| 090 | |a 659686 | ||
| 100 | |a 20190320d2018 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Optical excitation thermography for twill/plain weaves and stitched fabric dry carbon fibre preform inspection |f Zhang Hai [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 38 tit.] | ||
| 330 | |a Carbon fibres have become the natural choice as reinforcements for polymer composite materials (PMCs). The non-destructive inspection of dry carbon fibre preforms has the potential to increase the reproducibility and reduce the cost of PMC manufacturing, by identifying defects in dry multilayer preforms prior to resin injection. However, use of optical excitation thermography for inspecting dry carbon fibre preforms that constitute the structural reinforcement precursor in the manufacturing of PMCs is poorly documented in the open literature. In this work, optical excitation thermography was used for inspecting six dry multilayer carbon fibre preforms featuring different textile structures, thicknesses and defects, for the first time. Advanced image processing techniques were used in processing the thermographic data for comparative purposes. In particular, partial least square thermography, as a recently proposed technique, was studied in detail. Finally, the performance of different thermography techniques was analysed in terms of: (1) summarizing the capabilities of image diagnosis/processing techniques by signal-to-noise ratio analysis, and (2) identifying the monitoring modalities most suitable to industrial manufacturing. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | |t Composites Part A: Applied Science and Manufacturing | ||
| 463 | |t Vol. 107 |v [P. 282-293] |d 2018 | ||
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a optical excitation thermography | |
| 610 | 1 | |a non-destructive evaluation | |
| 610 | 1 | |a carbon fibre | |
| 610 | 1 | |a dry preform | |
| 610 | 1 | |a signal-to-noise ratio | |
| 610 | 1 | |a оптическое разрушение | |
| 610 | 1 | |a углеродные волокна | |
| 610 | 1 | |a сигнал-шум | |
| 701 | 0 | |a Zhang Hai | |
| 701 | 1 | |a Robitaille |b F. |g Francois | |
| 701 | 1 | |a Grosse |b C. U. |g Christian | |
| 701 | 1 | |a Ibarra-Castanedo |b C. |g Clemente | |
| 701 | 1 | |a Martins Jaime |b O. |g Ocana | |
| 701 | 1 | |a Sfarra |b S. |c specialist in the field of non-destructive testing |c Researcher of Tomsk Polytechnic University |f 1979- |g Stefano |3 (RuTPU)RU\TPU\pers\38660 | |
| 701 | 1 | |a Maldague |b X. |g Xavier | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Инженерная школа неразрушающего контроля и безопасности |b Центр промышленной томографии |b Научно-производственная лаборатория "Тепловой контроль" |3 (RuTPU)RU\TPU\col\23838 |
| 801 | 2 | |a RU |b 63413507 |c 20190320 |g RCR | |
| 856 | 4 | |u https://doi.org/10.1016/j.compositesa.2018.01.006 | |
| 942 | |c CF | ||