Pulse Cathodoluminescence of the Impurity Centers in Ceramics Based on the MgAl2O4 Spinel; Journal of Applied Spectroscopy; Vol. 85, iss. 3
| Parent link: | Journal of Applied Spectroscopy Vol. 85, iss. 3.— 2018.— [P. 416-421] |
|---|---|
| Altres autors: | , , , , , , , |
| Sumari: | Title screen The spectral and luminescence decay kinetics of magnesium aluminate spinel ceramics prepared by spark plasma sintering (SPS) and the starting nanopowders were studied. It was demonstrated that two types of luminescence in spinel ceramics can be observed after pulse e-beam excitation. The first type is due to intrinsic defects, and the second type due to Cr3+ and Mn2+ ions. It was shown that the luminescence decay kinetics for Cr3+ and Mn2+ impurity ions can be approximated by the sum of two exponents. The decay times for the Cr3+ ion are 35 and 409 ns, for the Mn2+ ion are 29 and 340 ns. High-temperature exposure during SPS synthesis does not lead to a change in the nearest surroundings of impurity ions. In the luminescence spectra of ceramic and powder samples the intensity ratio changes of intrinsic and impurity centers is associated with strong diffuse scattering of light for spinel nanopowders. Режим доступа: по договору с организацией-держателем ресурса |
| Idioma: | anglès |
| Publicat: |
2018
|
| Matèries: | |
| Accés en línia: | https://doi.org/10.1007/s10812-018-0666-9 |
| Format: | Electrònic Capítol de llibre |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=659363 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 659363 | ||
| 005 | 20251117145807.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\27913 | ||
| 090 | |a 659363 | ||
| 100 | |a 20190214d2018 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a US | ||
| 135 | |a drnn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Pulse Cathodoluminescence of the Impurity Centers in Ceramics Based on the MgAl2O4 Spinel |f E. F. Polisadova [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 20 tit.] | ||
| 330 | |a The spectral and luminescence decay kinetics of magnesium aluminate spinel ceramics prepared by spark plasma sintering (SPS) and the starting nanopowders were studied. It was demonstrated that two types of luminescence in spinel ceramics can be observed after pulse e-beam excitation. The first type is due to intrinsic defects, and the second type due to Cr3+ and Mn2+ ions. It was shown that the luminescence decay kinetics for Cr3+ and Mn2+ impurity ions can be approximated by the sum of two exponents. The decay times for the Cr3+ ion are 35 and 409 ns, for the Mn2+ ion are 29 and 340 ns. High-temperature exposure during SPS synthesis does not lead to a change in the nearest surroundings of impurity ions. In the luminescence spectra of ceramic and powder samples the intensity ratio changes of intrinsic and impurity centers is associated with strong diffuse scattering of light for spinel nanopowders. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | |t Journal of Applied Spectroscopy | ||
| 463 | |t Vol. 85, iss. 3 |v [P. 416-421] |d 2018 | ||
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a катодолюминесценция | |
| 610 | 1 | |a нанокерамика | |
| 610 | 1 | |a шпинель | |
| 610 | 1 | |a ионы | |
| 610 | 1 | |a спекание | |
| 701 | 1 | |a Polisadova |b E. F. |c specialist in the field of lighting engineering |c professor of Tomsk Polytechnic University, doctor of physical and mathematical sciences |f 1972- |g Elena Fyodorovna |3 (RuTPU)RU\TPU\pers\33900 |9 17473 | |
| 701 | 1 | |a Vaganov |b V. A. |c Specialist in the field of lightning engineering |c research engineer of Tomsk Polytechnic University |f 1991- |g Vitalii Andreevich |3 (RuTPU)RU\TPU\pers\37525 |9 20394 | |
| 701 | 1 | |a Stepanov |b S. A. |c specialist in the field of lightning engineering |c Engineer of Tomsk Polytechnic University |f 1986- |g Sergey Aleksandrovich |3 (RuTPU)RU\TPU\pers\33771 |9 17369 | |
| 701 | 1 | |a Paygin |b V. D. |c specialist in the field of material science |c engineer of Tomsk Polytechnic University |f 1992- |g Vladimir Denisovich |3 (RuTPU)RU\TPU\pers\38492 |9 20806 | |
| 701 | 1 | |a Khasanov |b O. L. |c Russian physicist, materials scientist, Doctor of Engineering |c professor, Director of TPU Nano-Centre and Head of the Department "Nanomaterials and Nanotechnologies" of TPU |f 1958- |g Oleg Leonidovich |3 (RuTPU)RU\TPU\pers\27102 |9 12652 | |
| 701 | 1 | |a Dvilis |b E. S. |c Chemical Engineer |c senior researcher of Tomsk Polytechnic University, Professor, doctor of physical and mathematical Sciences |f 1969- |g Edgar Sergeevich |3 (RuTPU)RU\TPU\pers\34597 |9 17959 | |
| 701 | 1 | |a Valiev |b D. T. |c specialist in the field of material science |c Associate Professor of Tomsk Polytechnic University, Candidate of Physical and Mathematical Sciences |f 1987- |g Damir Talgatovich |3 (RuTPU)RU\TPU\pers\33772 |9 17370 | |
| 701 | 1 | |a Kalinin |b R. |g Rostislav | |
| 801 | 2 | |a RU |b 63413507 |c 20190214 |g RCR | |
| 856 | 4 | |u https://doi.org/10.1007/s10812-018-0666-9 | |
| 942 | |c CF | ||