Modification of 40X13 steel at high-intensity nitrogen ion implantation; Journal of Physics: Conference Series; Vol. 1115 : 6th International Congress "Energy Fluxes and Radiation Effects". 14th International Conference on Modification of Materials with Particle Beams and Plasma Flows (14th CMM)
| Parent link: | Journal of Physics: Conference Series Vol. 1115 : 6th International Congress "Energy Fluxes and Radiation Effects". 14th International Conference on Modification of Materials with Particle Beams and Plasma Flows (14th CMM).— 2018.— [032053, 7 p.] |
|---|---|
| Korporativna značnica: | |
| Drugi avtorji: | , , , , |
| Izvleček: | Title screen This paper presents the results of the formation of deep modified layers in 40X13 steel using a high-intensity repetitively pulsed nitrogen ion beam with a current density up to 0.25 A/cm2. An arc generator with a hot cathode provided the DC nitrogen plasma flow. A plasma immersion approach was used for high-frequency, short-pulse very intense nitrogen ion beam formation. A grid hemisphere with radii of 7.5 cm was immersed in the plasma. Negative bias pulses with an amplitude of 1.2 kV, a pulse duration of 4 µs, and a pulse repetition rate of 105 pulses per second were applied to the grid. The substrates were implanted at the temperature of 500 °C and various processing times ranging from 20 to 120 minutes with 1.2 keV nitrogen ions using a very-high current density up to 0.25 A/cm2 ion beams. The work explores the surface morphology, elemental composition, and mechanical properties of deep-layer modified 40X13 steel after low ion energy, very-high-intensity nitrogen ion beam implantation. |
| Jezik: | angleščina |
| Izdano: |
2018
|
| Teme: | |
| Online dostop: | http://earchive.tpu.ru/handle/11683/57644 https://doi.org/10.1088/1742-6596/1115/3/032053 |
| Format: | Elektronski Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=659301 |
MARC
| LEADER | 00000naa2a2200000 4500 | ||
|---|---|---|---|
| 001 | 659301 | ||
| 005 | 20250917140612.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\27794 | ||
| 090 | |a 659301 | ||
| 100 | |a 20190131a2018 k y0engy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a GB | ||
| 105 | |a y z 100zy | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Modification of 40X13 steel at high-intensity nitrogen ion implantation |f A. I. Ryabchikov [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 9 tit.] | ||
| 330 | |a This paper presents the results of the formation of deep modified layers in 40X13 steel using a high-intensity repetitively pulsed nitrogen ion beam with a current density up to 0.25 A/cm2. An arc generator with a hot cathode provided the DC nitrogen plasma flow. A plasma immersion approach was used for high-frequency, short-pulse very intense nitrogen ion beam formation. A grid hemisphere with radii of 7.5 cm was immersed in the plasma. Negative bias pulses with an amplitude of 1.2 kV, a pulse duration of 4 µs, and a pulse repetition rate of 105 pulses per second were applied to the grid. The substrates were implanted at the temperature of 500 °C and various processing times ranging from 20 to 120 minutes with 1.2 keV nitrogen ions using a very-high current density up to 0.25 A/cm2 ion beams. The work explores the surface morphology, elemental composition, and mechanical properties of deep-layer modified 40X13 steel after low ion energy, very-high-intensity nitrogen ion beam implantation. | ||
| 461 | 1 | |0 (RuTPU)RU\TPU\network\3526 |t Journal of Physics: Conference Series | |
| 463 | 1 | |t Vol. 1115 : 6th International Congress "Energy Fluxes and Radiation Effects". 14th International Conference on Modification of Materials with Particle Beams and Plasma Flows (14th CMM) |o [proceedings], 16-22 September 2018, Tomsk, Russian Federation |d 2018 |v [032053, 7 p.] | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a модификации | |
| 610 | 1 | |a ионные пучки | |
| 610 | 1 | |a сталь | |
| 701 | 1 | |a Ryabchikov |b A. I. |c Professor of Tomsk Polytechnic University, Doctor of physical and mathematical sciences |c physicist |f 1950- |g Aleksandr Ilyich |3 (RuTPU)RU\TPU\pers\30912 | |
| 701 | 1 | |a Sivin |b D. O. |c physicist |c Senior researcher of Tomsk Polytechnic University, Candidate of technical sciences |f 1978- |g Denis Olegovich |3 (RuTPU)RU\TPU\pers\34240 | |
| 701 | 1 | |a Korneva |b O. S. |c physicist |c engineer of Tomsk Polytechnic University |f 1988- |g Olga Sergeevna |3 (RuTPU)RU\TPU\pers\37178 |9 20156 | |
| 701 | 1 | |a Ananin |b P. S. |c physicist |c senior researcher of Tomsk Polytechnic University, candidate of physical and mathematical sciences |f 1942- |g Petr Semenovich |3 (RuTPU)RU\TPU\pers\35673 | |
| 701 | 1 | |a Dektyarev |b S. V. |c physicist |c design engineer of Tomsk Polytechnic University |f 1957- |g Sergey Valentinovich |3 (RuTPU)RU\TPU\pers\35672 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Инженерная школа ядерных технологий |b Научная лаборатория высокоинтенсивной имплантации ионов |3 (RuTPU)RU\TPU\col\23698 |
| 801 | 2 | |a RU |b 63413507 |c 20200128 |g RCR | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/57644 | |
| 856 | 4 | |u https://doi.org/10.1088/1742-6596/1115/3/032053 | |
| 942 | |c CF | ||