Sintering and Mechanical Properties of Oxide-Oxide Composite Based on ZrO[2]-MgO Mixtures; AIP Conference Proceedings; Vol. 2051 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2018 (AMHS’18)

Sintering and Mechanical Properties of Oxide-Oxide Composite Based on ZrO[2]-MgO Mixtures; AIP Conference Proceedings; Vol. 2051 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2018 (AMHS’18)

Manylion Llyfryddiaeth
Parent link:AIP Conference Proceedings
Vol. 2051 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2018 (AMHS’18).— 2018.— [020046, 5 p.]
Awdur Corfforaethol: Национальный исследовательский Томский политехнический университет Инженерная школа новых производственных технологий Отделение материаловедения
Awduron Eraill: Buyakov A. S. Ales Sergeevich, Buyakova S. P. Svetlana Petrovna, Tkachev D. A., Kulkov S. N. Sergey Nikolaevich
Crynodeb:Title screen
Porous ceramics ZrO[2]-MgO with a 50 vol. % pore volume and bimodal pore size distribution were studied. The samples were produced by cold uniaxial pressing followed by sintering at temperature of 1600°C and a holding time from 10 min to 10 hours. Bimodal pore structure was obtained by adding of ultrahigh molecular weight polyethylene pore-forming particles with average size 50 [mu]m to the initial powder mixtures. The pore volume for all samples was constant-50 ± 3 vol. %. With increasing of sintering holding time the average size of the macropores decreased and the micropores increased. The coherent diffraction domains average size of components increases with increasing of MgO concentration and the time of the sintering, while the microdistortions of crystal lattice decrease. With an increase of the sintering holding time more than 5 hours, an insufficient stabilization of cubic ZrO[2] takes place for the low MgO concentrations. The dependences of the tensile strength and the Young's modulus on the microstresses in the ceramic composite structure are investigated. Estimation of the microstresses on the basis of X-ray diffraction analysis has shown that the tensile strength mainly determined by microstresses and its increasing leads to a strength decrease.
Режим доступа: по договору с организацией-держателем ресурса
Iaith:Saesneg
Cyhoeddwyd: 2018
Pynciau:
электронный ресурс
труды учёных ТПУ
спекание
механические свойства
композиты
смеси
пористая керамика
прессование
прочность
Mynediad Ar-lein:https://doi.org/10.1063/1.5083289
Fformat: Electronig Pennod Llyfr
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=659152