$Corundum Refractory Material in Alumina-Binder Resistant to High-Temperature Deformation; Refractories and Industrial Ceramics; Vol. 59, iss. 1$

Corundum Refractory Material in Alumina-Binder Resistant to High-Temperature Deformation; Refractories and Industrial Ceramics; Vol. 59, iss. 1

書誌詳細
Parent link:	Refractories and Industrial Ceramics Vol. 59, iss. 1.— 2018.— [P. 85-90]
団体著者:	Национальный исследовательский Томский политехнический университет Инженерная школа новых производственных технологий Научно-образовательный центр Н. М. Кижнера
その他の著者:	Pletnev P. M. Petr Michailovich, Pogrebenkov V. M. Valery Matveevich, Vereshchagin (Vereschagin, Vereshagin) V. I. Vladimir Ivanovich, Tyulkin D. S. Dmitry Sergeevich
要約:	Title screen In order to provide a good resistance for refractory structures towards high-temperature deformation during manufacture of engineering ceramic during firing at 1650°C a corundum refractory material is developed with a weight faction of more than 95 wt.% Al2O3. The ceramic binder used is high-temperature calcium hexa-aluminate formed during firing molded objects from a thixotropic mixture consisting of refractory filler of electromelted corundum and components for forming a binder, i.e., high-alumina cement (HAC) and finely ground alumina. Режим доступа: по договору с организацией-держателем ресурса
言語:	英語
出版事項:	2018
主題:	электронный ресурс труды учёных ТПУ calcium hexa-aluminate electromelted corundum thixotropic mixture alumina ceramic binder алюминат кальция тиксотропные горючие
オンライン･アクセス:	https://doi.org/10.1007/s11148-018-0187-3
フォーマット:	電子媒体図書の章
KOHA link:	https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=659077

その他の書誌記述
要約:	Title screen In order to provide a good resistance for refractory structures towards high-temperature deformation during manufacture of engineering ceramic during firing at 1650°C a corundum refractory material is developed with a weight faction of more than 95 wt.% Al2O3. The ceramic binder used is high-temperature calcium hexa-aluminate formed during firing molded objects from a thixotropic mixture consisting of refractory filler of electromelted corundum and components for forming a binder, i.e., high-alumina cement (HAC) and finely ground alumina. Режим доступа: по договору с организацией-держателем ресурса
DOI:	10.1007/s11148-018-0187-3