Correlation between structural and mechanical properties of RF magnetron sputter deposited hydroxyapatite coating
| Parent link: | Materials Characterization Vol. 142.— 2018.— [P. 261-269] |
|---|---|
| Autor Corporativo: | |
| Outros Autores: | , , , |
| Resumo: | Title screen In the present study hydroxyapatite (HA) thin films with a,b-plain and c-plain preferential orientation were prepared by means of RF-magnetron sputtering with water vapor addition into a working gas atmosphere to investigate the influence of microstructural features on mechanical performance of the coating at nanoscale. The mechanical properties of the HA coatings textured along a,b- and c-axes by nanoindentation conclusively highlight that elastic modulus, H/E ratio, H3/E2 parameter and percent of elastic recovery are determined by preferential orientation of the film. Nanoindentation reveals that the HA films exhibiting (300) texture possess commensurate nanohardness and lower elastic modulus compared to (002) oriented films, indicating that the former films possess higher resistance to cracking. The (002) and (300) textured coatings exhibited a nanohardness of 4.7?±?2.0?GPa and 4.4?±?2.2?GPa, respectively. The elastic modulus of the HA film with (300) and (002) preferential orientation was 75?±?40?GPa and 103?±?40?GPa, respectively. The HA coating with (300) texture showed a higher percentage of elastic recovery of 92% within unloading than that of the (002) textured film (69%). Режим доступа: по договору с организацией-держателем ресурса |
| Idioma: | inglês |
| Publicado em: |
2018
|
| Assuntos: | |
| Acesso em linha: | https://doi.org/10.1016/j.matchar.2018.05.042 |
| Formato: | Recurso Eletrônico Capítulo de Livro |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=658967 |
| Resumo: | Title screen In the present study hydroxyapatite (HA) thin films with a,b-plain and c-plain preferential orientation were prepared by means of RF-magnetron sputtering with water vapor addition into a working gas atmosphere to investigate the influence of microstructural features on mechanical performance of the coating at nanoscale. The mechanical properties of the HA coatings textured along a,b- and c-axes by nanoindentation conclusively highlight that elastic modulus, H/E ratio, H3/E2 parameter and percent of elastic recovery are determined by preferential orientation of the film. Nanoindentation reveals that the HA films exhibiting (300) texture possess commensurate nanohardness and lower elastic modulus compared to (002) oriented films, indicating that the former films possess higher resistance to cracking. The (002) and (300) textured coatings exhibited a nanohardness of 4.7?±?2.0?GPa and 4.4?±?2.2?GPa, respectively. The elastic modulus of the HA film with (300) and (002) preferential orientation was 75?±?40?GPa and 103?±?40?GPa, respectively. The HA coating with (300) texture showed a higher percentage of elastic recovery of 92% within unloading than that of the (002) textured film (69%). Режим доступа: по договору с организацией-держателем ресурса |
|---|---|
| DOI: | 10.1016/j.matchar.2018.05.042 |