Influence of Mechanical Treatment on Consolidation Processes of Ultradisperse Powders of Stabilized Zirconium Oxide; Inorganic Materials: Applied Research; Vol. 9, iss. 2
| Parent link: | Inorganic Materials: Applied Research.— , 2010- Vol. 9, iss. 2.— 2018.— [P. 343–346] |
|---|---|
| Päätekijä: | |
| Yhteisötekijä: | |
| Yhteenveto: | Title screen The effect of preliminary machining of ultradisperse powders of stabilized zirconium dioxide and its composite on consolidation in compacts under uniaxial static pressing and subsequent sintering is studied. The investigations were carried out with powders of compositions (in mol %) 97ZrO2–3Y2O3 and 80Al2O3–20(ZrO2–Y), which were obtained by the sol-gel and the plasma-chemical method, respectively. Mechanical processing of powders was carried out in two ways. The first method consisted in preliminary static pressing of powders at elevated pressure of 900 MPa and their subsequent grinding in a ball mill. The second method consisted in grinding the initial powders in an Activator-2SL planetary mill with drums and grinding balls of zirconia. It is established that mechanical treatment significantly affects the density of compacts. In this case, there is no strict correlation between the density of the sintered ceramic and the density of compacts. With increasing density of compacts, their expansion can be observed at the isothermal holding stage, which leads to a decrease in density of the ceramic. It is shown that, in dry grinding to improve the technological properties of ultradisperse powders obtained by the sol-gel and plasma-chemical methods, the most suitable is the method of mechanical treatment, which consists in pre-pressing the powders at elevated pressure and then grinding them in a ball mill. Режим доступа: по договору с организацией-держателем ресурса |
| Kieli: | englanti |
| Julkaistu: |
2018
|
| Aiheet: | |
| Linkit: | https://doi.org/10.1134/S2075113318020119 |
| Aineistotyyppi: | Elektroninen Kirjan osa |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=658397 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 658397 | ||
| 005 | 20250205143635.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\26148 | ||
| 090 | |a 658397 | ||
| 100 | |a 20181010d2018 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a US | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Influence of Mechanical Treatment on Consolidation Processes of Ultradisperse Powders of Stabilized Zirconium Oxide |f S. A. Gyngazov (Ghyngazov) | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: p. 346 (16 tit.)] | ||
| 330 | |a The effect of preliminary machining of ultradisperse powders of stabilized zirconium dioxide and its composite on consolidation in compacts under uniaxial static pressing and subsequent sintering is studied. The investigations were carried out with powders of compositions (in mol %) 97ZrO2–3Y2O3 and 80Al2O3–20(ZrO2–Y), which were obtained by the sol-gel and the plasma-chemical method, respectively. Mechanical processing of powders was carried out in two ways. The first method consisted in preliminary static pressing of powders at elevated pressure of 900 MPa and their subsequent grinding in a ball mill. The second method consisted in grinding the initial powders in an Activator-2SL planetary mill with drums and grinding balls of zirconia. It is established that mechanical treatment significantly affects the density of compacts. In this case, there is no strict correlation between the density of the sintered ceramic and the density of compacts. With increasing density of compacts, their expansion can be observed at the isothermal holding stage, which leads to a decrease in density of the ceramic. It is shown that, in dry grinding to improve the technological properties of ultradisperse powders obtained by the sol-gel and plasma-chemical methods, the most suitable is the method of mechanical treatment, which consists in pre-pressing the powders at elevated pressure and then grinding them in a ball mill. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | |t Inorganic Materials: Applied Research |d 2010- | ||
| 463 | |t Vol. 9, iss. 2 |v [P. 343–346] |d 2018 | ||
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a порошки | |
| 610 | 1 | |a цирконий | |
| 610 | 1 | |a прессование | |
| 610 | 1 | |a спекание | |
| 700 | 1 | |a Gyngazov (Ghyngazov) |b S. A. |c specialist in the field of electronics |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1958- |g Sergey Anatolievich |3 (RuTPU)RU\TPU\pers\33279 |9 17024 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Институт неразрушающего контроля (ИНК) |b Проблемная научно-исследовательская лаборатория электроники, диэлектриков и полупроводников (ПНИЛ ЭДиП) |3 (RuTPU)RU\TPU\col\19033 |
| 801 | 2 | |a RU |b 63413507 |c 20181010 |g RCR | |
| 856 | 4 | |u https://doi.org/10.1134/S2075113318020119 | |
| 942 | |c CF | ||