Influence of long-term operation on structure, fatigue durability and impact toughness of 09Mn2Si pipe steel; Procedia Structural Integrity; Vol. 5 : 2nd International Conference on Structural Integrity, ICSI 2017, 4-7 September 2017, Funchal, Madeira, Portugal
| Parent link: | Procedia Structural Integrity Vol. 5 : 2nd International Conference on Structural Integrity, ICSI 2017, 4-7 September 2017, Funchal, Madeira, Portugal.— 2017.— [P. 401-408] |
|---|---|
| Körperschaft: | |
| Weitere Verfasser: | , , , , , , , , |
| Zusammenfassung: | Title screen A comprehensive study of the structure, mechanical properties including impact toughness of 09Mn2Si steel used for constructing main gas pipeline” Mastakh-Berge-Yakutsk” after 37 years of operation was carried out. A comparative analysis of the results obtained for the emergency stock steel was conducted. It is shown that long-term operation does not give rise to a substantial redistribution of cementite. Deformation aging is slightly expressed and is manifested through the precipitation of finely dispersed carbides in the grain bulk. The revealed structure degradation does not practically make sense under static tension or hardness measurement. At the same time, under cyclic testing the microstructure degradation being occurred during long-term operation results in fatigue lifetime decrease especially at the stage of crack initiation. The most pronounced manifestation of structure changes is related to decreasing impact toughness of 09Mn2Si steel which reaches ~ 2 times under negative temperatures. The reasons and mechanisms of the observed phenomena are discussed. Режим доступа: по договору с организацией-держателем ресурса |
| Sprache: | Englisch |
| Veröffentlicht: |
2017
|
| Schlagworte: | |
| Online-Zugang: | https://doi.org/10.1016/j.prostr.2017.07.188 |
| Format: | Elektronisch Buchkapitel |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=657198 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 657198 | ||
| 005 | 20250623134535.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\23700 | ||
| 035 | |a RU\TPU\network\23092 | ||
| 090 | |a 657198 | ||
| 100 | |a 20180117d2017 k||y0engy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a NL | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Influence of long-term operation on structure, fatigue durability and impact toughness of 09Mn2Si pipe steel |f S. V. Panin [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: p. 408 (13 tit.)] | ||
| 330 | |a A comprehensive study of the structure, mechanical properties including impact toughness of 09Mn2Si steel used for constructing main gas pipeline” Mastakh-Berge-Yakutsk” after 37 years of operation was carried out. A comparative analysis of the results obtained for the emergency stock steel was conducted. It is shown that long-term operation does not give rise to a substantial redistribution of cementite. Deformation aging is slightly expressed and is manifested through the precipitation of finely dispersed carbides in the grain bulk. The revealed structure degradation does not practically make sense under static tension or hardness measurement. At the same time, under cyclic testing the microstructure degradation being occurred during long-term operation results in fatigue lifetime decrease especially at the stage of crack initiation. The most pronounced manifestation of structure changes is related to decreasing impact toughness of 09Mn2Si steel which reaches ~ 2 times under negative temperatures. The reasons and mechanisms of the observed phenomena are discussed. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | |t Procedia Structural Integrity | ||
| 463 | |t Vol. 5 : 2nd International Conference on Structural Integrity, ICSI 2017, 4-7 September 2017, Funchal, Madeira, Portugal |v [P. 401-408] |d 2017 | ||
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a microstructure degradation | |
| 610 | 1 | |a embrittlement | |
| 610 | 1 | |a impact toughness | |
| 610 | 1 | |a fatigue durability | |
| 610 | 1 | |a трубы | |
| 610 | 1 | |a усталостная прочность | |
| 610 | 1 | |a ударопрочность | |
| 610 | 1 | |a стали | |
| 701 | 1 | |a Panin |b S. V. |c specialist in the field of material science |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1971- |g Sergey Viktorovich |3 (RuTPU)RU\TPU\pers\32910 |9 16758 | |
| 701 | 1 | |a Vlasov |b I. V. |c specialist in the field of material science |c Engineer of Tomsk Polytechnic University |f 1988- |g Ilya Viktorovich |3 (RuTPU)RU\TPU\pers\33560 | |
| 701 | 1 | |a Marushchak |b P. O. |g Pavel Orestovich | |
| 701 | 1 | |a Eremin |b A. V. |c specialist in the field of material science |c Engineer of Tomsk Polytechnic University |f 1990- |g Alexandr Vyacheslavovich |3 (RuTPU)RU\TPU\pers\32912 | |
| 701 | 1 | |a Byakov |b A. V. |c specialist in the field of material science |c engineer of Tomsk polytechnical university, Candidate of Technical Sciences |f 1985- |g Anton Viktorovich |3 (RuTPU)RU\TPU\pers\35461 | |
| 701 | 1 | |a Berto |b F. |g Filippo | |
| 701 | 1 | |a Vinogradov |b A. Y. |g Aleksey Yurjevich | |
| 701 | 1 | |a Syromyatnikova |b A. S. |g Aytalina Stepanovna | |
| 701 | 1 | |a Stankevich |b R. V. |g Roman Vladimirovich | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Институт физики высоких технологий (ИФВТ) |b Кафедра материаловедения в машиностроении (ММС) |3 (RuTPU)RU\TPU\col\18688 |
| 801 | 0 | |a RU |b 63413507 |c 20180117 |g RCR | |
| 850 | |a 63413507 | ||
| 856 | 4 | |u https://doi.org/10.1016/j.prostr.2017.07.188 | |
| 942 | |c CF | ||