Wear of Nitrogen Ion Implanted Copper with Tribological Cu-Mo-S Coatings; AIP Conference Proceedings; Vol. 1909 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2017 (AMHS’17)

Manylion Llyfryddiaeth
Parent link:	AIP Conference Proceedings Vol. 1909 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2017 (AMHS’17).— 2017.— [020238, 4 p.]
Awdur Corfforaethol:	Национальный исследовательский Томский политехнический университет
Awduron Eraill:	Zharkov S. Yu. Stanislav, Sergeev V. P. Viktor Petrovich, Sungatulin A. R. Alfred, Kalashnikov M. P. Mark Petrovich
Crynodeb:	Title screen The paper studies the effect of nitrogen ion implantation in copper samples before depositing a solid lubricant Cu-Mo-S coating on their wear resistance during wear testing in pairs with a copper counterface in the argon atmosphere. It was found that wear resistance of samples with Cu-Mo-S coating decreased with the increase in fluence of nitrogen ion implantation. Режим доступа: по договору с организацией-держателем ресурса
Iaith:	Saesneg
Cyhoeddwyd:	2017
Pynciau:	электронный ресурс труды учёных ТПУ износ трибологические свойства покрытия ионная имплантация медь твердые смазки износостойкость transition tribology ion
Mynediad Ar-lein:	https://doi.org/10.1063/1.5013919
Fformat:	Electronig Pennod Llyfr
KOHA link:	https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=657185

Disgrifiad
Crynodeb:	Title screen The paper studies the effect of nitrogen ion implantation in copper samples before depositing a solid lubricant Cu-Mo-S coating on their wear resistance during wear testing in pairs with a copper counterface in the argon atmosphere. It was found that wear resistance of samples with Cu-Mo-S coating decreased with the increase in fluence of nitrogen ion implantation. Режим доступа: по договору с организацией-держателем ресурса