Investigation of the Change in the Phase Composition, Properties, and Hydraulic Activity During the Thermal Treatment of Magnesian Materials
| Parent link: | Refractories and Industrial Ceramics Vol. 58, iss. 3.— 2017.— [P. 331-337] |
|---|---|
| Autor principal: | |
| Autor corporatiu: | |
| Altres autors: | |
| Sumari: | Title screen The effect of the heat treatment regime on the hydraulic activity of magnesian materials was determined from the heat release during interaction with water. Hydration processes proceed efficiently, hardening structures are formed after calcination of the initial magnesian materials in the range of 500 – 800°C. Therefore, in the production of hydraulically active magnesium oxide used to make the magnesian binder, it is necessary to bake magnesian materials regardless of their nature at low or moderate temperatures in the range of 500 – 800°C. The change in the structure and properties of magnesian materials during heat treatment has a great influence on the processes of sintering refractory materials. Режим доступа: по договору с организацией-держателем ресурса |
| Idioma: | anglès |
| Publicat: |
2017
|
| Matèries: | |
| Accés en línia: | https://doi.org/10.1007/s11148-017-0105-0 |
| Format: | Electrònic Capítol de llibre |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=656720 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 656720 | ||
| 005 | 20250404162509.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\23186 | ||
| 090 | |a 656720 | ||
| 100 | |a 20171208d2017 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a US | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Investigation of the Change in the Phase Composition, Properties, and Hydraulic Activity During the Thermal Treatment of Magnesian Materials |f N. A. Mitina, V. A. Lotov | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: p. 336-337 (20 tit.)] | ||
| 330 | |a The effect of the heat treatment regime on the hydraulic activity of magnesian materials was determined from the heat release during interaction with water. Hydration processes proceed efficiently, hardening structures are formed after calcination of the initial magnesian materials in the range of 500 – 800°C. Therefore, in the production of hydraulically active magnesium oxide used to make the magnesian binder, it is necessary to bake magnesian materials regardless of their nature at low or moderate temperatures in the range of 500 – 800°C. The change in the structure and properties of magnesian materials during heat treatment has a great influence on the processes of sintering refractory materials. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | |t Refractories and Industrial Ceramics | ||
| 463 | |t Vol. 58, iss. 3 |v [P. 331-337] |d 2017 | ||
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a magnesian materials | |
| 610 | 1 | |a magnesium oxide | |
| 610 | 1 | |a heat treatment | |
| 610 | 1 | |a specific surface area | |
| 610 | 1 | |a phase composition | |
| 610 | 1 | |a hydraulic activity | |
| 610 | 1 | |a магнезиальные материалы | |
| 610 | 1 | |a термообработка | |
| 610 | 1 | |a оксид магния | |
| 610 | 1 | |a фазовый состав | |
| 610 | 1 | |a гидравлическая активность | |
| 700 | 1 | |a Mitina |b N. A. |c Chemical Engineer |c Associate Professor of Tomsk Polytechnic University, Candidate of technical sciences |f 1974- |g Nataliya Aleksandrovna |3 (RuTPU)RU\TPU\pers\35929 |9 19070 | |
| 701 | 1 | |a Lotov |b V. A. |c Chemical Engineer |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1942- |g Vasiliy Agafonovich |3 (RuTPU)RU\TPU\pers\35928 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Институт физики высоких технологий (ИФВТ) |b Кафедра технологии силикатов и наноматериалов (ТСН) |3 (RuTPU)RU\TPU\col\18694 |
| 801 | 2 | |a RU |b 63413507 |c 20171220 |g RCR | |
| 856 | 4 | |u https://doi.org/10.1007/s11148-017-0105-0 | |
| 942 | |c CF | ||