Structural-phase changes in hard alloy WC-steel 110G13 after dynamic loading; Russian Physics Journal; Vol. 37, iss. 8

Structural-phase changes in hard alloy WC-steel 110G13 after dynamic loading; Russian Physics Journal; Vol. 37, iss. 8

Dades bibliogràfiques
Parent link:Russian Physics Journal
Vol. 37, iss. 8.— 1993.— [P. 757-761]
Altres autors: Paul A. V., Gnyusov S. F. Sergey Fedorovich, Ivanov Yu. F. Yuriy Fedorovich, Kulkov S. N. Sergey Nikolaevich, Kozlov E. V.
Sumari:Title screen
The methods of optical and electron diffraction microscopy are used to study the evolution of phase composition and defect structure in hard alloy WC-steel 100G13 after dynamic loading. Both stable and metastable austenite (the binding phase) are seen in the alloy after such loading. The martensitic transformation ? ? e is seen along with slip in the case of the metastable state, which makes it possible to significantly reduce the scale of plastic deformation of the binder and redistribute the external load onto particles of the reinforcing phase. Microcracks form a special structure in this case, and the integrity of the specimen is maintained up to high loading rates.
Режим доступа: по договору с организацией-держателем ресурса
Idioma:anglès
Publicat: 1993
Matèries:
электронный ресурс
труды учёных ТПУ
структурно-фазовые изменения
твердые сплавы
сталь
Accés en línia:https://link.springer.com/article/10.1007/BF00559871
Format: Electrònic Capítol de llibre
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=655832

Ítems similars

Ítems similars