High-rate deformation and spall fracture of hadfield steel under action of high-current nanosecond relativistic electron beam; Technical Physics Letters; Vol. 36, iss. 9

High-rate deformation and spall fracture of hadfield steel under action of high-current nanosecond relativistic electron beam; Technical Physics Letters; Vol. 36, iss. 9

Bibliographic Details
Parent link:Technical Physics Letters: Scientific Journal
Vol. 36, iss. 9.— 2010.— [P. 801-803]
Corporate Author: Национальный исследовательский Томский политехнический университет (ТПУ) Энергетический институт (ЭНИН) Кафедра автоматизации теплоэнергетических процессов (АТП)
Other Authors: Gnyusov S. F. Sergey Fedorovich, Rotshtein V. P., Polevin S. D., Kitsanov S. A.
Summary:Title screen
Features of the plastic deformation and dynamic spall fracture of Hadfield steel under conditions of shock wave loading at a straining rate of ~106 s-1 have been studied. The shock load (~30 GPa, ~0.2 µs) was produced by pulses of a SINUS-7 electron accelerator, which generated relativistic electron bunches with an electron energy of up to 1.35 MeV, a duration of 45 ns, and a peak power on the target of 3.4 Ч 1010 W/cm2. It is established that the spalling proceeds via mixed viscous-brittle intergranular fracture, unlike the cases of quasi-static tensile and impact loading, where viscous transgranular fracture is typical. It is shown that the intergranular character of the spall fracture is caused by the localization of plastic deformation at grain boundaries containing precipitated carbide inclusions.
Режим доступа: по договору с организацией-держателем ресурса
Language:English
Published: 2010
Subjects:
электронный ресурс
труды учёных ТПУ
электронные пучки
сталь
деформация
Online Access:http://dx.doi.org/10.1134/S1063785010090087
Format: Electronic Book Chapter
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=655557

Similar Items

Similar Items