Effect of Ultradisperse TiO2, ZrO2, and Cryolite Powders on High-Chromium Cast Iron Hardening; Bulletin of the Russian Academy of Sciences: Physics; Vol. 80, iss. 11
| Parent link: | Bulletin of the Russian Academy of Sciences: Physics.— , 2007- Vol. 80, iss. 11.— 2016.— [P. 1317–1321] |
|---|---|
| Συγγραφή απο Οργανισμό/Αρχή: | |
| Άλλοι συγγραφείς: | , , , |
| Περίληψη: | Title screen The quantitative parameters of structural-phase state of Fe-27% Cr-2% Ni-2.8% C cast iron are determined via X-ray diffraction and transmission electron microscopy before and after adding ultradisperse TiO2, ZrO2 and cryolite powders. The contributions from individual physical mechanisms in increasing the yield stress of cast irons are quantitatively assessed. It is established that the main contribution to the durability of modified Fe-27% Cr-2% Ni-2.8% C cast iron come from solid-solution, dispersion, and grainboundary mechanisms of hardening. Режим доступа: по договору с организацией-держателем ресурса |
| Γλώσσα: | Αγγλικά |
| Έκδοση: |
2016
|
| Θέματα: | |
| Διαθέσιμο Online: | http://dx.doi.org/10.3103/S1062873816110319 |
| Μορφή: | Ηλεκτρονική πηγή Κεφάλαιο βιβλίου |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=654411 |