Friction and wear behavior of polydicyclopentadiene under dry sliding and boundary lubrication; Petroleum and Coal; Vol. 58, iss. 5
| Parent link: | Petroleum and Coal Vol. 58, iss. 5.— 2016.— [P. 556-560] |
|---|---|
| Corporate Authors: | , |
| Andre forfattere: | , , , , , |
| Summary: | Title screen In this investigation the influence of test load and roughness of steel on the friction and wear behaviour of polydicyclopentadiene (PDCPD) were studied. Friction and wear tests of PDCPD and R6M5 steel were carried out under dry friction and boundary lubrication on a pin-on-disc arran-gement. Tribological tests were performed at room temperature at different pressures (10 N and 18 N), the different roughness of steel (0.08 µm and 0.15 µm), sliding speed 0.5 m/s and sliding distance 3500 m. It is shown that under dry friction sliding, the wear increases with increasing pressure. In addition to this, decreasing of the roughness of steel from 0.15 µm to 0.08 µm reduces the wear intensity more than 2.0 times. It was found that in the presence of boundary lubrication friction coefficients are significantly reduced linearly with the decrease in viscosity of lubricants (polydimethylsiloxane fluids). Свободный доступ из сети Интернет |
| Sprog: | engelsk |
| Udgivet: |
2016
|
| Fag: | |
| Online adgang: | http://www.vurup.sk/wp-content/uploads/dlm_uploads/2017/07/pc_6_2016_zamanova_486cor.pdf |
| Format: | Electronisk Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=653526 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 653526 | ||
| 005 | 20250917135643.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\18998 | ||
| 090 | |a 653526 | ||
| 100 | |a 20170311d2016 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a SK | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Friction and wear behavior of polydicyclopentadiene under dry sliding and boundary lubrication |f M. K. Zamanova, V. I. Kutsuk, V. G. Bondaletov [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: p. 559-560 (18 tit.)] | ||
| 330 | |a In this investigation the influence of test load and roughness of steel on the friction and wear behaviour of polydicyclopentadiene (PDCPD) were studied. Friction and wear tests of PDCPD and R6M5 steel were carried out under dry friction and boundary lubrication on a pin-on-disc arran-gement. Tribological tests were performed at room temperature at different pressures (10 N and 18 N), the different roughness of steel (0.08 µm and 0.15 µm), sliding speed 0.5 m/s and sliding distance 3500 m. It is shown that under dry friction sliding, the wear increases with increasing pressure. In addition to this, decreasing of the roughness of steel from 0.15 µm to 0.08 µm reduces the wear intensity more than 2.0 times. It was found that in the presence of boundary lubrication friction coefficients are significantly reduced linearly with the decrease in viscosity of lubricants (polydimethylsiloxane fluids). | ||
| 333 | |a Свободный доступ из сети Интернет | ||
| 461 | |t Petroleum and Coal | ||
| 463 | |t Vol. 58, iss. 5 |v [P. 556-560] |d 2016 | ||
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a полидициклопентадиен | |
| 610 | 1 | |a полимеризация | |
| 610 | 1 | |a коэффициент трения | |
| 610 | 1 | |a граничная смазка | |
| 701 | 1 | |a Zamanova |b M. K. |c Chemical Engineer |c engineer of Tomsk Polytechnic University |f 1983- |g Margarita Karimovna |3 (RuTPU)RU\TPU\pers\33834 | |
| 701 | 1 | |a Kutsuk |b V. I. |g Viorika Ivanovna | |
| 701 | 1 | |a Bondaletov |b V. G. |c Chemical Engineer |c Professor of Tomsk Polytechnic University, Doctor of Technical Sciences |f 1957- |g Vladimir Grigoryevich |3 (RuTPU)RU\TPU\pers\31989 |9 16049 | |
| 701 | 1 | |a Korneva |b O. S. |c physicist |c engineer of Tomsk Polytechnic University |f 1988- |g Olga Sergeevna |3 (RuTPU)RU\TPU\pers\37178 |9 20156 | |
| 701 | 1 | |a Shulepov |b I. A. |c physicist |c Engineer-designer of Tomsk Polytechnic University, Candidate of physical and mathematical sciences |f 1954- |g Ivan Anisimovich |3 (RuTPU)RU\TPU\pers\33092 | |
| 701 | 1 | |a Rusakov |b D. |g Dmitrii | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Институт природных ресурсов (ИПР) |b Кафедра технологии органических веществ и полимерных материалов (ТОВПМ) |3 (RuTPU)RU\TPU\col\18659 |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Физико-технический институт (ФТИ) |b Центр измерений свойств материалов (ЦИСМ) |3 (RuTPU)RU\TPU\col\19361 |
| 801 | 2 | |a RU |b 63413507 |c 20200217 |g RCR | |
| 856 | 4 | |u http://www.vurup.sk/wp-content/uploads/dlm_uploads/2017/07/pc_6_2016_zamanova_486cor.pdf | |
| 942 | |c CF | ||