Structural and Phase Transformations in 0.3С-1Cr-1Mn-1Si-Fe Steel after Electrolytic Plasma Treatment; AIP Conference Proceedings; Vol. 1783 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016

Structural and Phase Transformations in 0.3С-1Cr-1Mn-1Si-Fe Steel after Electrolytic Plasma Treatment; AIP Conference Proceedings; Vol. 1783 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016

Bibliografske podrobnosti
Parent link:AIP Conference Proceedings
Vol. 1783 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016.— 2016.— [020112, 4 p.]
Corporate Authors: Национальный исследовательский Томский политехнический университет (ТПУ) Институт социально-гуманитарных технологий (ИСГТ), Томский политехнический университет
Drugi avtorji: Kozlov E. Eduard, Popova N. Natalya, Zhurerova L. Lyaila, Nikonenko E. L. Elena Leonidovna, Kalashnikov M. P. Mark Petrovich, Skakov M. Mazhin
Izvleček:Title screen
The paper presents the transmission electron microscopy (TEM) investigations on thin foils concerning phase transitions occurred in the type 0.3С-1Cr-1Mn-1Si-Fe alloyed steel after the electrolyte plasma treatment, i.e. carbonitriding at 850°С during 5 min. TEM investigations involve two points, namely: on the specimen surface and at 50 [mu]m distance from the surface, i.e. in transition layer. It is shown that carbonitriding results in the formation of structures the properties of which are changed at a distance from it's the specimen surface. Thus, the modified morphology of the steel matrix is represented mostly by high-temperature lamellar martensite on [alpha]-phase surface, while the intermediate layer is represented by massive martensite. After carbonitriding, the particles of the alloyed cementite and М[2]С[0.61]N[0.39], М[4](С,N), М[7](С,N)[3], M[23](C,N)[6] carbonitrides are observed in all layers inside [alpha]-phase crystals and at their boundaries. The concentration of carbon and nitrogen on the surface is considerably higher. The modification of quantity is observed in the distribution and the volume fraction of carbide phases with the distance from the specimen surface, while the amount of carbonitride phases significantly reduces. Also, it is shown that carbonitriding leads to a complete relaxation of the internal local stresses on the specimen surface, while in the intermediate layer plastic stresses are observed.
Режим доступа: по договору с организацией-держателем ресурса
Jezik:angleščina
Izdano: 2016
Teme:
электронный ресурс
труды учёных ТПУ
структурные превращения
фазовые превращения
плазменная обработка
просвечивающая электронная микроскопия
ПЭМ
фольга
Online dostop:http://dx.doi.org/10.1063/1.4966405
Format: Elektronski Book Chapter
KOHA link:https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=652697

Podobne knjige/članki

Podobne knjige/članki