Effect of Mechanical Activation on the Phase Composition of Lanthanum Hexaboride Produced by SHS Method; Indian Journal of Science and Technology; Vol. 8, iss. 36

Chi tiết về thư mục
Parent link:	Indian Journal of Science and Technology Vol. 8, iss. 36.— 2016.— [4 p.]
Tác giả của công ty:	Национальный исследовательский Томский политехнический университет (ТПУ) Физико-технический институт (ФТИ) Кафедра физико-энергетических установок (№ 21) (ФЭУ)
Tác giả khác:	Dolmatov O. Yu. Oleg Yurevich, Kolyadko D. K. Daniil Konstantinovich, Kuznetsov M. S. Mikhail Sergeyevich, Chursin S. S. Stanislav Sergeevich
Tóm tắt:	Title screen Background/Objectives: The work considers the effect of mechanical activation of the charge on the phase composition of the final product based on lanthanum hexaboride produced by the method of self-propagating high-temperature synthesis. Methods/Statistical analysis: To study the influence of mechanical activation on the SHS process a mixture of the following reagents was taken: Lanthanum oxide La2O3 and amorphous boron in the mass fractions of 2 to 1 respectively. Mechanical activation was carried out on a planetary ball mill AGO-2S. Findings: The mechanical activation results in particle size reduction, but it has a “saturation threshold”. Optimal parameters of mechanical activation are selected for the most complete conversion of the charge to the desired product of lanthanum hexaboride. It is established that mechanical activation has a “saturation threshold” after which further processing does not bring positive results, the sample either undergoes a thermo-mechanical destruction or the sample is converted to the finished product incompletely, so it is necessary to select the parameters of mechanical activation for each reagent mixture (charge). Optimal average particle size of the charge - 2.52 ?m (activation mode with a frequency of 20 Hz and a processing time of 15 minutes) was defined experimentally at which the most complete conversion of the sample to the finished product occurs. Applications/ Improvements: Due to the development of accelerator equipment for various purposes, the main direction of the development of thermal cathodes is the provision of good emission characteristics in harsh environments
Ngôn ngữ:	Tiếng Anh
Được phát hành:	2016
Những chủ đề:	электронный ресурс труды учёных ТПУ гексаборид лантана механическая активация фазовый состав ускорительное оборудование самораспространяющийся высокотемпературный синтез
Truy cập trực tuyến:	http://dx.doi.org/10.17485/ijst%2F2015%2Fv8i36%2F90572
Định dạng:	Điện tử Chương của sách
KOHA link:	https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=652687