Tensile Strength on Friction Stir Processed AMg5 (5083) Aluminum Alloy
| Parent link: | AIP Conference Proceedings Vol. 1783 : Advanced Materials with Hierarchical Structure for New Technologies and Reliable Structures 2016.— 2016.— [020027, 4 p.] |
|---|---|
| Інші автори: | , , , , |
| Резюме: | Title screen The results of the tensile tests carried out both on AMg5 (5083) aluminum alloy samples base and those obtained using friction stir processing technique are reported. The tensile test samples have been prepared from the friction stir processed plates so that their tensile axis was parallel to the processing direction. The maximum tensile strength of the processed samples was 9% higher than of the base metal. The fractographic examination shows the presence of flat areas inherent of the brittle fracture in all three friction processed samples. The load-extension curves show that friction stir processing may suppress the serrated yielding. Режим доступа: по договору с организацией-держателем ресурса |
| Мова: | Англійська |
| Опубліковано: |
2016
|
| Предмети: | |
| Онлайн доступ: | http://dx.doi.org/10.1063/1.4966320 |
| Формат: | Електронний ресурс Частина з книги |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=652608 |
| Резюме: | Title screen The results of the tensile tests carried out both on AMg5 (5083) aluminum alloy samples base and those obtained using friction stir processing technique are reported. The tensile test samples have been prepared from the friction stir processed plates so that their tensile axis was parallel to the processing direction. The maximum tensile strength of the processed samples was 9% higher than of the base metal. The fractographic examination shows the presence of flat areas inherent of the brittle fracture in all three friction processed samples. The load-extension curves show that friction stir processing may suppress the serrated yielding. Режим доступа: по договору с организацией-держателем ресурса |
|---|---|
| DOI: | 10.1063/1.4966320 |