Secondary polyvinyl butyral modified with potassium polytitanate for coatings with improved mechanical properties; AIP Conference Proceedings; Vol. 1772 : Prospects of Fundamental Sciences Development (PFSD-2016)
| Parent link: | AIP Conference Proceedings Vol. 1772 : Prospects of Fundamental Sciences Development (PFSD-2016).— 2016.— [030013, 7 p.] |
|---|---|
| Tác giả của công ty: | |
| Tác giả khác: | , , , , , , |
| Tóm tắt: | Title screen The technology of laminated glass is accompanied with a large amount of polyvinyl butyral wastes, which are used for recycling due to mechanical properties of recycled PVB as these properties are lower than those of the original polymer. The properties of composite coatings based on secondary polyvinyl butyral modified with potassium polytitanate were investigated. The composite coating was obtained by polyvinyl butyral dissolved in ethyl alcohol and then dispersed potassium polytitanate into a solution. The resulting suspension was poured onto the surface of a solid substrate and then dried. The research shows that the surface modification of potassium polytitanate with different coupling agents significantly improves the polymer composite mechanical properties. The investigation of various homogenization techniques established a possibility for a significant improvement in the properties of a polyvinyl butyral composite by treatment in a ball mill. The mechanism interactions among the coupling agents, binders, and surface fillers were determined. The research also highlights the possibility of secondary polyvinyl butyral recycling and the production of films with high mechanical properties. Режим доступа: по договору с организацией-держателем ресурса |
| Ngôn ngữ: | Tiếng Anh |
| Được phát hành: |
2016
|
| Loạt: | Materials structure and properties under modification |
| Những chủ đề: | |
| Truy cập trực tuyến: | http://dx.doi.org/10.1063/1.4964551 http://earchive.tpu.ru/handle/11683/34997 |
| Định dạng: | Điện tử Chương của sách |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=652105 |
MARC
| LEADER | 00000nla2a2200000 4500 | ||
|---|---|---|---|
| 001 | 652105 | ||
| 005 | 20251126142736.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\17368 | ||
| 035 | |a RU\TPU\network\17366 | ||
| 090 | |a 652105 | ||
| 100 | |a 20161201a2016 k y0engy50 ba | ||
| 101 | 0 | |a eng | |
| 105 | |a y z 100zy | ||
| 135 | |a drgn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Secondary polyvinyl butyral modified with potassium polytitanate for coatings with improved mechanical properties |f I. Burmistrov [et al.] | |
| 203 | |a Text |c electronic | ||
| 225 | 1 | |a Materials structure and properties under modification | |
| 300 | |a Title screen | ||
| 320 | |a [References: 26 tit.] | ||
| 330 | |a The technology of laminated glass is accompanied with a large amount of polyvinyl butyral wastes, which are used for recycling due to mechanical properties of recycled PVB as these properties are lower than those of the original polymer. The properties of composite coatings based on secondary polyvinyl butyral modified with potassium polytitanate were investigated. The composite coating was obtained by polyvinyl butyral dissolved in ethyl alcohol and then dispersed potassium polytitanate into a solution. The resulting suspension was poured onto the surface of a solid substrate and then dried. The research shows that the surface modification of potassium polytitanate with different coupling agents significantly improves the polymer composite mechanical properties. The investigation of various homogenization techniques established a possibility for a significant improvement in the properties of a polyvinyl butyral composite by treatment in a ball mill. The mechanism interactions among the coupling agents, binders, and surface fillers were determined. The research also highlights the possibility of secondary polyvinyl butyral recycling and the production of films with high mechanical properties. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | 0 | |0 (RuTPU)RU\TPU\network\4816 |t AIP Conference Proceedings | |
| 463 | 0 | |0 (RuTPU)RU\TPU\network\17119 |t Vol. 1772 : Prospects of Fundamental Sciences Development (PFSD-2016) |o XIII International Conference of Students and Young Scientists, 26–29 April 2016, Tomsk, Russia |o [proceedings] |f National Research Tomsk Polytechnic University (TPU) ; eds. A. Yu. Godymchuk (Godimchuk) ; L. Rieznichenko |v [030013, 7 p.] |d 2016 | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a покрытия | |
| 610 | 1 | |a механические свойства | |
| 610 | 1 | |a композиционные покрытия | |
| 610 | 1 | |a стекла | |
| 610 | 1 | |a отходы | |
| 610 | 1 | |a переработка | |
| 610 | 1 | |a пленки | |
| 701 | 1 | |a Burmistrov |b I. |g Igor | |
| 701 | 1 | |a Panova |b L. |g Lydia | |
| 701 | 1 | |a Yusupov |b Kh. |g Khabib | |
| 701 | 1 | |a Ermolenko |b A. |g Anna | |
| 701 | 1 | |a Yakovlev |b E. |g Egor | |
| 701 | 1 | |a Godymchuk (Godimchuk) |b A. Yu. |c specialist in the field of nanotechnologies and nanomaterials |c Associate Professor of Tomsk Polytechnic University, candidate of technical science |f 1978- |g Anna Yuryevna |3 (RuTPU)RU\TPU\pers\29602 |9 14137 | |
| 701 | 1 | |a Yudintseva |b T. |g Tamara | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |c (2009- ) |9 26305 |
| 801 | 2 | |a RU |b 63413507 |c 20170120 |g RCR | |
| 856 | 4 | |u http://dx.doi.org/10.1063/1.4964551 | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/34997 | |
| 942 | |c CF | ||