Low-temperature CO oxidation on Ag/ZSM-5 catalysts: Influence of Si/Al ratio and redox pretreatments on formation of silver active sites; Fuel; Vol. 188
| Parent link: | Fuel Vol. 188.— 2016.— [P. 121-131] |
|---|---|
| Korporativna značnica: | |
| Drugi avtorji: | , , , , , , , , |
| Izvleček: | Title screen Silver catalysts supported on ZSM-5 (Si/Al = 30, 50 and 80) were investigated for low-temperature CO oxidation to study the nature of the silver active sites and their formation under the influence of the support chemical composition and redox pretreatments. The catalysts were characterized by HRTEM, FTIR, XPS, diffuse reflectance UV–Vis spectroscopy, NH3 thermodesorption (NH3 TPD) and temperature-programmed reduction (H2 TPR). The chemical composition (Si/Al ratio) of the ZSM-5 zeolite support significantly affects catalytic properties of Ag/ZSM-5 samples: the lower the Broensted acidity of the zeolite support, the higher the activity of the catalysts. Interestingly, while oxidizing pretreatment of catalysts led to a significantly better performance than reducing pretreatments, the consecutive reducing treatment of the preoxidized samples significantly promoted the catalytic activity for low-temperature CO oxidation. Thus, Ag/ZMS-5 catalyst with Si/Al = 80, pretreated consecutively in oxidizing and reducing conditions, showed the highest activity, reaching 90% CO conversion at just 40 °C. Comparison of activity and characterization results showed that silver particles with size below 2 nm are the most active; larger particles are just “spectators”. The most probable silver active centers in the low-temperature CO oxidation are ionic species, mostly charged clusters Agn?+, strongly interacting with the support. The obtained results in low-temperature CO oxidation might be of particular interest for neutralization of exhaust gases of car engines during “cold start”. Режим доступа: по договору с организацией-держателем ресурса |
| Jezik: | angleščina |
| Izdano: |
2016
|
| Teme: | |
| Online dostop: | http://dx.doi.org/10.1016/j.fuel.2016.10.037 |
| Format: | Elektronski Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=651605 |
MARC
| LEADER | 00000naa0a2200000 4500 | ||
|---|---|---|---|
| 001 | 651605 | ||
| 005 | 20250324111744.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\16854 | ||
| 090 | |a 651605 | ||
| 100 | |a 20161117d2016 k||y0rusy50 ba | ||
| 101 | 0 | |a eng | |
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Low-temperature CO oxidation on Ag/ZSM-5 catalysts: Influence of Si/Al ratio and redox pretreatments on formation of silver active sites |f E. N. Kolobova [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 62 tit.] | ||
| 330 | |a Silver catalysts supported on ZSM-5 (Si/Al = 30, 50 and 80) were investigated for low-temperature CO oxidation to study the nature of the silver active sites and their formation under the influence of the support chemical composition and redox pretreatments. The catalysts were characterized by HRTEM, FTIR, XPS, diffuse reflectance UV–Vis spectroscopy, NH3 thermodesorption (NH3 TPD) and temperature-programmed reduction (H2 TPR). The chemical composition (Si/Al ratio) of the ZSM-5 zeolite support significantly affects catalytic properties of Ag/ZSM-5 samples: the lower the Broensted acidity of the zeolite support, the higher the activity of the catalysts. Interestingly, while oxidizing pretreatment of catalysts led to a significantly better performance than reducing pretreatments, the consecutive reducing treatment of the preoxidized samples significantly promoted the catalytic activity for low-temperature CO oxidation. Thus, Ag/ZMS-5 catalyst with Si/Al = 80, pretreated consecutively in oxidizing and reducing conditions, showed the highest activity, reaching 90% CO conversion at just 40 °C. Comparison of activity and characterization results showed that silver particles with size below 2 nm are the most active; larger particles are just “spectators”. The most probable silver active centers in the low-temperature CO oxidation are ionic species, mostly charged clusters Agn?+, strongly interacting with the support. The obtained results in low-temperature CO oxidation might be of particular interest for neutralization of exhaust gases of car engines during “cold start”. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | |t Fuel | ||
| 463 | |t Vol. 188 |v [P. 121-131] |d 2016 | ||
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a низкие температуры | |
| 610 | 1 | |a окисление | |
| 610 | 1 | |a серебряные катализаторы | |
| 701 | 1 | |a Kolobova |b E. N. |c Chemical Engineer |c design engineer of Tomsk Polytechnic University |f 1989- |g Ekaterina Nikolaevna |3 (RuTPU)RU\TPU\pers\34488 |9 17871 | |
| 701 | 1 | |a Pestryakov |b A. N. |c Chemist |c Professor of Tomsk Polytechnic University, Doctor of Chemical Science |f 1963- |g Aleksey Nikolaevich |3 (RuTPU)RU\TPU\pers\30471 |9 14796 | |
| 701 | 1 | |a Mamontov |b G. V. |g Grigory Vladimirovich | |
| 701 | 1 | |a Kotolevich |b Yu. I. |g Yuliya I. | |
| 701 | 1 | |a Bogdanchikova |b N. E. |g Nina Evgenjevna | |
| 701 | 1 | |a Farias |g M. H. | |
| 701 | 1 | |a Vosmerikov |c Aleksandr V. |g A. V. | |
| 701 | 1 | |a Vosmerikova |c Lyudmila V. |g L. V. | |
| 701 | 1 | |a Cortes |c Corberan V. |g C. V. | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет |b Энергетический институт |b Кафедра автоматизации теплоэнергетических процессов |3 (RuTPU)RU\TPU\col\18678 |9 27131 |
| 801 | 2 | |a RU |b 63413507 |c 20170908 |g RCR | |
| 856 | 4 | |u http://dx.doi.org/10.1016/j.fuel.2016.10.037 | |
| 942 | |c CF | ||