Textural Characteristics of Products Obtained by Electrochemical Oxidation of Copper and Cadmium Using Alternating Current; Key Engineering Materials; Vol. 712 : Advanced Materials for Technical and Medical Purpose (AMTMP 2016)
| Parent link: | Key Engineering Materials: Scientific Journal Vol. 712 : Advanced Materials for Technical and Medical Purpose (AMTMP 2016).— 2016.— [P. 112-116] |
|---|---|
| Autor corporatiu: | , |
| Altres autors: | , , , , , |
| Sumari: | Title screen The porous structures of nanoparticles of copper and cadmium prepared by AC electrochemical synthesis in solutions of acetate of sodium, chlorides of ammonium and sodium were studied. It is established that at current density of 1A/cm{2} and concentration of NaCl 3 % wt. with the highest specific surface area (8.23m{2}/g), maximum pore volume (0.029 cm{3}/g) are formed, and the largest volume of the particles is characteristic of the nominal pore diameter - 62 nm. The values of specific surface area and total pore volume with increase in the temperature of calcination decrease, and the pores are slightly enlarged in diameter. Thus, the obtained data allow predicting operating parameters of the electrolysis to obtain copper - cadmium oxide system a predetermined porous structure. Режим доступа: по договору с организацией-держателем ресурса |
| Idioma: | anglès |
| Publicat: |
2016
|
| Col·lecció: | Electrophysical and Electrochemical Methods and Technologies of Materials Treatment |
| Matèries: | |
| Accés en línia: | http://dx.doi.org/10.4028/www.scientific.net/KEM.712.112 |
| Format: | Electrònic Capítol de llibre |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=651269 |
MARC
| LEADER | 00000nla2a2200000 4500 | ||
|---|---|---|---|
| 001 | 651269 | ||
| 005 | 20241211093243.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\16518 | ||
| 035 | |a RU\TPU\network\16514 | ||
| 090 | |a 651269 | ||
| 100 | |a 20161108a2016 k y0engy50 ba | ||
| 101 | 0 | |a eng | |
| 105 | |a y z 100zy | ||
| 135 | |a drgn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Textural Characteristics of Products Obtained by Electrochemical Oxidation of Copper and Cadmium Using Alternating Current |f A. S. Dolinina [et al.] | |
| 203 | |a Text |c electronic | ||
| 225 | 1 | |a Electrophysical and Electrochemical Methods and Technologies of Materials Treatment | |
| 300 | |a Title screen | ||
| 330 | |a The porous structures of nanoparticles of copper and cadmium prepared by AC electrochemical synthesis in solutions of acetate of sodium, chlorides of ammonium and sodium were studied. It is established that at current density of 1A/cm{2} and concentration of NaCl 3 % wt. with the highest specific surface area (8.23m{2}/g), maximum pore volume (0.029 cm{3}/g) are formed, and the largest volume of the particles is characteristic of the nominal pore diameter - 62 nm. The values of specific surface area and total pore volume with increase in the temperature of calcination decrease, and the pores are slightly enlarged in diameter. Thus, the obtained data allow predicting operating parameters of the electrolysis to obtain copper - cadmium oxide system a predetermined porous structure. | ||
| 333 | |a Режим доступа: по договору с организацией-держателем ресурса | ||
| 461 | 0 | |0 (RuTPU)RU\TPU\network\11477 |t Key Engineering Materials |o Scientific Journal | |
| 463 | 0 | |0 (RuTPU)RU\TPU\network\16425 |t Vol. 712 : Advanced Materials for Technical and Medical Purpose (AMTMP 2016) |o The Workshop , February 15-17, 2016, Tomsk, Russia |o [proceedings] |f National Research Tomsk Polytechnic University (TPU) ; eds. G. E. Osokin [et al.] |v [P. 112-116] |d 2016 | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a текстурные характеристики | |
| 610 | 1 | |a электрохимическое окисление | |
| 610 | 1 | |a медь | |
| 610 | 1 | |a кадмий | |
| 610 | 1 | |a переменный ток | |
| 610 | 1 | |a пористые структуры | |
| 610 | 1 | |a наночастицы | |
| 610 | 1 | |a электролиз | |
| 701 | 1 | |a Dolinina |b A. S. |g Alesya Sergeevna |f 1987- |c Chemical Engineer |c Associate Professor, Leading Expert of Tomsk Polytechnic University, Candidate of Technical Sciences |y Tomsk |3 (RuTPU)RU\TPU\pers\33893 |9 17466 | |
| 701 | 1 | |a Korobochkin |b V. V. |c Chemical Engineer |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1951- |g Valery Vasilievich |3 (RuTPU)RU\TPU\pers\31050 | |
| 701 | 1 | |a Usoltseva |b N. V. |c Chemical Engineer |c Engineer of Tomsk Polytechnic University |f 1985- |g Natalia Vasilievna |3 (RuTPU)RU\TPU\pers\31509 |9 15670 | |
| 701 | 1 | |a Sudarev |b E. A. |g Evgeniy Aleksandrovich |f 1986- |c Chemical Engineer |c Associate Professor of Tomsk Polytechnic University, Candidate of technical Sciences |y Tomsk |3 (RuTPU)RU\TPU\pers\34619 |9 17981 | |
| 701 | 1 | |a Bikbaeva |b A. V. |g Alena | |
| 701 | 1 | |a Popov |b M. V. |g Maxim | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Институт физики высоких технологий (ИФВТ) |b Кафедра общей химии и химической технологии (ОХХТ) |3 (RuTPU)RU\TPU\col\21253 |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Институт физики высоких технологий (ИФВТ) |b Кафедра технологии силикатов и наноматериалов (ТСН) |3 (RuTPU)RU\TPU\col\18694 |
| 801 | 2 | |a RU |b 63413507 |c 20170120 |g RCR | |
| 856 | 4 | |u http://dx.doi.org/10.4028/www.scientific.net/KEM.712.112 | |
| 942 | |c CF | ||