Composite materials based on high-modulus compounds for additive technology; IOP Conference Series: Materials Science and Engineering; Vol. 140 : Interdisciplinary Problems in Additive Technologies
| Parent link: | IOP Conference Series: Materials Science and Engineering Vol. 140 : Interdisciplinary Problems in Additive Technologies.— 2016.— [012009, 11 p.] |
|---|---|
| 共著者: | , |
| その他の著者: | , , , |
| 要約: | Title screen The effect of adding nanocrystalline ZrO[2] and submicron TiC to ultrafine Al[2]O[3] on mechanical properties and the microstructure of the composites developed by hot pressing was investigated. It was shown that by means of hot pressing in argon atmosphere at the sintering temperature of 1500 °C one can obtain the composites of Al[2]O[3]-ZrO[2]-TiC with a fine structure and minimal porosity. It was shown that in the material a multi-scale hierarchical structure is formed, which possesses high physical and mechanical properties: the hardness and fracture toughness was 22 GPa and 5.2 MPa*m1/2, respectively. It has been shown that mechanical properties of the composite are better than those of commercial composites based on aluminum oxide (Al[2]O[3], ZTA, Al[2]O[3]-TiC) and are comparable to those of silicon nitride. |
| 言語: | 英語 |
| 出版事項: |
2016
|
| 主題: | |
| オンライン･アクセス: | http://dx.doi.org/10.1088/1757-899X/140/1/012009 http://earchive.tpu.ru/handle/11683/34863 |
| フォーマット: | 電子媒体 図書の章 |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=650714 |