The influence of ZrB[2]-SiC powders mechanical treatment on the structure of sintered ceramic composites
| Parent link: | IOP Conference Series: Materials Science and Engineering Vol. 140 : Interdisciplinary Problems in Additive Technologies.— 2016.— [012006, 4 p.] |
|---|---|
| Autor corporatiu: | |
| Altres autors: | , , , , |
| Sumari: | Title screen The effect of mechanical treatment by planetary ball milling on the properties of hot pressed ZrB[2] - SiC ceramics was studied. It was shown that material densification after mechanical treatment is finished at initial stages of sintering process. Addition of SiC leads to an essential increase of sample density to 99% of theoretically achievable for powder with 2% of SiC, as compared with ZrB[2] with the density less than 76%. It was demonstrated that all defects that were accumulated during mechanical treatment are annealed during hot pressing, and there are no changes of CDD values in sintered. |
| Idioma: | anglès |
| Publicat: |
2016
|
| Matèries: | |
| Accés en línia: | http://dx.doi.org/10.1088/1757-899X/140/1/012006 http://earchive.tpu.ru/handle/11683/34989 |
| Format: | Electrònic Capítol de llibre |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=650699 |
MARC
| LEADER | 00000nla2a2200000 4500 | ||
|---|---|---|---|
| 001 | 650699 | ||
| 005 | 20240128190814.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\15948 | ||
| 035 | |a RU\TPU\network\15940 | ||
| 090 | |a 650699 | ||
| 100 | |a 20161017a2016 k y0engy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a GB | ||
| 105 | |a y z 100zy | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a The influence of ZrB[2]-SiC powders mechanical treatment on the structure of sintered ceramic composites |f S. P. Buyakova [et al.] | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 5 tit.] | ||
| 330 | |a The effect of mechanical treatment by planetary ball milling on the properties of hot pressed ZrB[2] - SiC ceramics was studied. It was shown that material densification after mechanical treatment is finished at initial stages of sintering process. Addition of SiC leads to an essential increase of sample density to 99% of theoretically achievable for powder with 2% of SiC, as compared with ZrB[2] with the density less than 76%. It was demonstrated that all defects that were accumulated during mechanical treatment are annealed during hot pressing, and there are no changes of CDD values in sintered. | ||
| 461 | 0 | |0 (RuTPU)RU\TPU\network\2008 |t IOP Conference Series: Materials Science and Engineering | |
| 463 | 0 | |0 (RuTPU)RU\TPU\network\15930 |t Vol. 140 : Interdisciplinary Problems in Additive Technologies |o International Seminar, 16–17 December 2015, Tomsk, Russia |o [proceedings] |v [012006, 4 p.] |d 2016 | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a порошки | |
| 610 | 1 | |a механическая обработка | |
| 610 | 1 | |a структуры | |
| 610 | 1 | |a спеченные композиты | |
| 610 | 1 | |a керамические композиты | |
| 610 | 1 | |a горячее прессование | |
| 701 | 1 | |a Buyakova |b S. P. |c specialist in the field of material science |c Professor of Tomsk Polytechnic University, Doctor of technical sciences |f 1968- |g Svetlana Petrovna |3 (RuTPU)RU\TPU\pers\34758 |9 18108 | |
| 701 | 1 | |a Burlachenko |b A. | |
| 701 | 1 | |a Mirovoi |b Yu. | |
| 701 | 1 | |a Sevostiyanova |b I. | |
| 701 | 1 | |a Kulkov |b S. N. |c specialist in the field of material science |c Professor of Tomsk Polytechnic University, Doctor of physical and mathematical sciences |f 1952- |g Sergey Nikolaevich |3 (RuTPU)RU\TPU\pers\31428 | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Институт физики высоких технологий (ИФВТ) |b Кафедра материаловедения в машиностроении (ММС) |3 (RuTPU)RU\TPU\col\18688 |
| 801 | 2 | |a RU |b 63413507 |c 20170120 |g RCR | |
| 856 | 4 | |u http://dx.doi.org/10.1088/1757-899X/140/1/012006 | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/34989 | |
| 942 | |c CF | ||