The effect of hydrogen on strain hardening and fracture mechanism of high-nitrogen austenitic steel; IOP Conference Series: Materials Science and Engineering; Vol. 140 : Interdisciplinary Problems in Additive Technologies
| Parent link: | IOP Conference Series: Materials Science and Engineering Vol. 140 : Interdisciplinary Problems in Additive Technologies.— 2016.— [012005, 6 p.] |
|---|---|
| সংস্থা লেখক: | |
| অন্যান্য লেখক: | , , , , , , |
| সংক্ষিপ্ত: | Title screen High-nitrogen austenitic steels are perspective materials for an electron-beam welding and for producing of wear-resistant coatings, which can be used for application in aggressive atmospheres. The tensile behavior and fracture mechanism of high-nitrogen austenitic steel Fe-20Cr-22Mn-1.5V-0.2C-0.6N (in wt.%) after electrochemical hydrogen charging for 2, 10 and 40 hours have been investigated. Hydrogenation of steel provides a loss of yield strength, uniform elongation and tensile strength. The degradation of tensile properties becomes stronger with increase in charging duration - it occurs more intensive in specimens hydrogenated for 40 hours as compared to ones charged for 2-10 hours. Fracture analysis reveals a hydrogen-induced formation of brittle surface layers up to 6 [mu]m thick after 40 hours of saturation. Hydrogenation changes fracture mode of steel from mixed intergranular-transgranular to mainly transgranular one. |
| ভাষা: | ইংরেজি |
| প্রকাশিত: |
2016
|
| বিষয়গুলি: | |
| অনলাইন ব্যবহার করুন: | http://dx.doi.org/10.1088/1757-899X/140/1/012005 http://earchive.tpu.ru/handle/11683/34988 |
| বিন্যাস: | বৈদ্যুতিক গ্রন্থের অধ্যায় |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=650691 |
| সংক্ষিপ্ত: | Title screen High-nitrogen austenitic steels are perspective materials for an electron-beam welding and for producing of wear-resistant coatings, which can be used for application in aggressive atmospheres. The tensile behavior and fracture mechanism of high-nitrogen austenitic steel Fe-20Cr-22Mn-1.5V-0.2C-0.6N (in wt.%) after electrochemical hydrogen charging for 2, 10 and 40 hours have been investigated. Hydrogenation of steel provides a loss of yield strength, uniform elongation and tensile strength. The degradation of tensile properties becomes stronger with increase in charging duration - it occurs more intensive in specimens hydrogenated for 40 hours as compared to ones charged for 2-10 hours. Fracture analysis reveals a hydrogen-induced formation of brittle surface layers up to 6 [mu]m thick after 40 hours of saturation. Hydrogenation changes fracture mode of steel from mixed intergranular-transgranular to mainly transgranular one. |
|---|---|
| ডিওআই: | 10.1088/1757-899X/140/1/012005 |