Effects of Inert Nanoparticles of High-Melting-Point Compositions on Grain Structure and Strength of Ni[3]Al Intermetallic Compounds; IOP Conference Series: Materials Science and Engineering; Vol. 142 : Innovative Technologies in Engineering
| Parent link: | IOP Conference Series: Materials Science and Engineering Vol. 142 : Innovative Technologies in Engineering.— 2016.— [012083, 6 p.] |
|---|---|
| Main Author: | |
| Corporate Author: | |
| Other Authors: | , |
| Summary: | Title screen The paper represents experimental findings both in the area of effects of nanoparticles of inert high-melting-point TiN compounds on a Ni[3]Al intermetallic grain structure creation in the conditions of high temperature synthesis under pressure, and in the area of impact of grain structure modification on intermetallic compounds' strength factor temperature dependence. It was demonstrated that appending a stoichiometric composition of nanosized particles of high-melting-point inert chemical compounds (TiN) initiates a manyfold loss of average size of grain of Ni[3]Al intermetallic compounds, synthesized under pressure, as well as a sufficient intermetallic compounds' strength rise within a wide range of temperatures (up to 1 000 degree C). Electron-microscopic evaluations of a synthesized intermetallic structure with TiN nanoparticles, showed that, during the process of intermetallic polycrystalline structure creation from high temperature synthesis products melts, TiN nanoparticles are mainly spread throughout the boundaries and joints of grain structure, acting as stoppers of grain boundaries migration. |
| Language: | English |
| Published: |
2016
|
| Subjects: | |
| Online Access: | http://dx.doi.org/10.1088/1757-899X/142/1/012083 http://earchive.tpu.ru/handle/11683/34757 |
| Format: | Electronic Book Chapter |
| KOHA link: | https://koha.lib.tpu.ru/cgi-bin/koha/opac-detail.pl?biblionumber=650448 |
MARC
| LEADER | 00000nla2a2200000 4500 | ||
|---|---|---|---|
| 001 | 650448 | ||
| 005 | 20231102025723.0 | ||
| 035 | |a (RuTPU)RU\TPU\network\15666 | ||
| 035 | |a RU\TPU\network\15665 | ||
| 090 | |a 650448 | ||
| 100 | |a 20161006a2016 k y0engy50 ba | ||
| 101 | 0 | |a eng | |
| 102 | |a GB | ||
| 105 | |a y z 100zy | ||
| 135 | |a drcn ---uucaa | ||
| 181 | 0 | |a i | |
| 182 | 0 | |a b | |
| 200 | 1 | |a Effects of Inert Nanoparticles of High-Melting-Point Compositions on Grain Structure and Strength of Ni[3]Al Intermetallic Compounds |f V. E. Ovcharenko, E. N. Boyangin, V. A. Chudinov | |
| 203 | |a Text |c electronic | ||
| 300 | |a Title screen | ||
| 320 | |a [References: 12 tit.] | ||
| 330 | |a The paper represents experimental findings both in the area of effects of nanoparticles of inert high-melting-point TiN compounds on a Ni[3]Al intermetallic grain structure creation in the conditions of high temperature synthesis under pressure, and in the area of impact of grain structure modification on intermetallic compounds' strength factor temperature dependence. It was demonstrated that appending a stoichiometric composition of nanosized particles of high-melting-point inert chemical compounds (TiN) initiates a manyfold loss of average size of grain of Ni[3]Al intermetallic compounds, synthesized under pressure, as well as a sufficient intermetallic compounds' strength rise within a wide range of temperatures (up to 1 000 degree C). Electron-microscopic evaluations of a synthesized intermetallic structure with TiN nanoparticles, showed that, during the process of intermetallic polycrystalline structure creation from high temperature synthesis products melts, TiN nanoparticles are mainly spread throughout the boundaries and joints of grain structure, acting as stoppers of grain boundaries migration. | ||
| 461 | 0 | |0 (RuTPU)RU\TPU\network\2008 |t IOP Conference Series: Materials Science and Engineering | |
| 463 | 0 | |0 (RuTPU)RU\TPU\network\15319 |t Vol. 142 : Innovative Technologies in Engineering |o VII International Scientific Practical Conference, 19–21 May 2016, Yurga, Russian Federation |o [proceedings] |v [012083, 6 p.] |d 2016 | |
| 610 | 1 | |a электронный ресурс | |
| 610 | 1 | |a труды учёных ТПУ | |
| 610 | 1 | |a наночастицы | |
| 610 | 1 | |a плавление | |
| 610 | 1 | |a интерметаллиды | |
| 610 | 1 | |a олово | |
| 610 | 1 | |a высокотемпературный синтез | |
| 700 | 1 | |a Ovcharenko |b V. E. |c specialist in the field of mechanical engineering |c Professor-consultant of Yurga technological Institute of Tomsk Polytechnic University, doctor of technical sciences |f 1945- |g Vladimir Efimovich |2 stltpush |3 (RuTPU)RU\TPU\pers\32423 |9 16372 | |
| 701 | 1 | |a Boyangin |b E. N. | |
| 701 | 1 | |a Chudinov |b V. A. | |
| 712 | 0 | 2 | |a Национальный исследовательский Томский политехнический университет (ТПУ) |b Юргинский технологический институт (филиал) (ЮТИ) |b Кафедра технологии машиностроения (ТМС) |h 356 |2 stltpush |3 (RuTPU)RU\TPU\col\18902 |
| 801 | 2 | |a RU |b 63413507 |c 20170120 |g RCR | |
| 856 | 4 | |u http://dx.doi.org/10.1088/1757-899X/142/1/012083 | |
| 856 | 4 | |u http://earchive.tpu.ru/handle/11683/34757 | |
| 942 | |c CF | ||